PEI ULTEM™ HU1010-1H1000 SABIC INNOVATIVE US

Unit Price:
$31029 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Middle flow Biocompatibility Steam sterilization
Application Areas:Medical and nursing suppl Medical devices
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	1.3	%
	Moisture Absorption	Equilibrium, 23°C	ASTM D570	1.3	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%
Melt Mass-Flow Rate	337°C/6.6 kg	ASTM D1238	18	g/10 min
Melt Volume flow Rate	360°C/5.0 kg	ISO 1133	25.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 6, 7	ISO 178	160	Mpa
	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	174	Mpa
	Flexural Stress	Flexural Stress	Yield, 100 mm Span 5	ASTM D790	165	Mpa
Tensile Strength	Yield 3	ASTM D638	110	Mpa
	Tensile Strength	Yield	ISO 527-2/5	105	Mpa
	Tensile Strength	Tensile Strength	Break 3	ASTM D638	105	Mpa
Tensile Modulus	-- 2	ASTM D638	3580	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	3200	Mpa
Tensile Elongation	Yield 3	ASTM D638	7.0	%
	Tensile Elongation	Yield	ISO 527-2/5	6.0	%
		Tensile Elongation	Break 3	ASTM D638	60	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/5	60	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	3420	Mpa
	Flexural Modulus	100 mm Span 5	ASTM D790	3510	Mpa
	Flexural Modulus	Flexural Modulus	-- 6	ISO 178	3300	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Thermal Conductivity		ASTM C177	0.22	W/m/K
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Vicat Softening Temperature	--	ASTM D152510	218	°C
	Vicat Softening Temperature	--	ISO 306/B50	211	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	212	°C
Linear thermal expansion coefficient	Flow : -20 to 150°C	ASTM E831	5.6E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : -40 to 40°C	ISO 11359-2	5.0E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	5.0E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	5.0E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	207	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	198	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	193	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	1.60 mm, in Air	ASTM D149	33	KV/mm
Dielectric Strength	Dielectric Strength	1.60 mm, in Oil	ASTM D149	28	KV/mm
Comparative Tracking Index		UL 746	PLC 4
Hot-wire Ignition		UL 746	PLC 1
High Voltage Arc Tracking Rate		UL 746	PLC 2
High Amp Arc Ignition		UL 746	PLC 3
Arc Resistance		ASTM D495	PLC 5
Dissipation Factor?	1 kHz	ASTM D150	1.3E-3
Dissipation Factor?	Dissipation Factor?	2.45 GHz	ASTM D150	2.5E-3
Dielectric Constant	1 kHz	ASTM D150	3.15
Volume Resistivity		ASTM D257	1.0E+17	ohms·cm

Injection	Test Result	Unit
Drying Temperature	150	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	350 到 400	°C
Mold Temperature	135 到 165	°C
Drying Time	4.0 到 6.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	330 到 400	°C
Middle Temperature	340 到 400	°C
Front Temperature	345 到 400	°C
Nozzle Temperature	345 到 400	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Gardner Impact	23°C	ASTM D3029	33.0	J
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	33.0	J
Reverse Notch Izod Impact	3.20 mm	ASTM D256	1200	J/m
Unnotched Izod Impact Strength	23°C	ASTM D4812	1300	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	109

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ASTM D2863	44	%
Flame Rating	0.71 mm	UL 94	V-2
	Flame Rating	0.75 mm	UL 94	V-0
	Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.