PEI ULTEM™ 1000-1000 SABIC INNOVATIVE US
188
- Unit Price:
- $22328 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 66.9MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant enhance
- Application Areas:Electrical field Electronic field Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 24 hr | ASTM D570 | 0.25 | % |
| Equilibrium, 23°C | ASTM D570 | 1.3 | % | |
| Melt Mass-Flow Rate | 337°C/6.6 kg | ASTM D1238 | 9.0 | g/10 min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Yield | ASTM D638 | 7.0 | % |
| Break | ASTM D638 | 60 | % | |
| Tensile Strength | Yield | ASTM D638 | 110 | Mpa |
| Tensile Modulus | ASTM D638 | 3580 | Mpa | |
| Poisson Ratio | ASTM E132 | 0.36 | ||
| Flexural Modulus | 100 mm Span | ASTM D790 | 3510 | Mpa |
| Flexural Strength | Yield, 100 mm Span | ASTM D790 | 165 | Mpa |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 10.0 | mg |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal Conductivity | ASTM C177 | 0.22 | W/m/K | |
| RTI | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI Elec | UL 746 | 170 | °C | |
| Linear thermal expansion coefficient | Flow : -20 to 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| Across Flow : -20 to 150°C | ASTM E831 | 5.4E-5 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 210 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 201 | °C | |
| Vicat Softening Temperature | ASTM D15254 | 218 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc Resistance | ASTM D495 | PLC 5 | ||
| High Amp Arc Ignition | UL 746 | PLC 3 | ||
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 | ||
| Comparative Tracking Index | UL 746 | PLC 4 | ||
| Hot-wire Ignition | UL 746 | PLC 1 | ||
| Dielectric Strength | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm | |
| 3.20 mm, in Oil | ASTM D149 | 20 | KV/mm | |
| Dielectric Constant | 100 Hz | ASTM D150 | 3.15 | |
| 1 kHz | ASTM D150 | 3.15 | ||
| Volume Resistivity | ASTM D257 | 1.0E+17 | ohms·cm | |
| Dissipation Factor? | 100 Hz | ASTM D150 | 1.5E-3 | |
| 1 kHz | ASTM D150 | 1.2E-3 | ||
| 2.45 GHz | ASTM D150 | 2.5E-3 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 330 到 400 | °C | ||
| Middle Temperature | 340 到 400 | °C | ||
| Front Temperature | 345 到 400 | °C | ||
| Nozzle Temperature | 345 到 400 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.025 到 0.076 | mm | ||
| Drying Temperature | 150 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 350 到 400 | °C | ||
| Mold Temperature | 135 到 165 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner Impact | 23°C | ASTM D3029 | 36.0 | J |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1300 | J/m |
| Reverse Notch Izod Impact | 3.20 mm | ASTM D256 | 1300 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Scale | ASTM D785 | 109 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ASTM D2863 | 47 | % | |
| Flame Rating | 0.40 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.