PEEK KetaSpire® PEEK KT-820GF30 SOLVAY USA

Unit Price:
$84393 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:high strength Chemical resistance Steam sterilization Fatigue resistance Dimensional stability High temperature resistan High rigidity
Application Areas:film Electronic and Electrical Aircraft Applications Connector Automotive Applications Dental applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24hr	ASTMD570	0.10	%
Melt Mass-Flow Rate	400°C/2.16kg	ASTMD1238	0.70	g/10min
Modeling Shrinkage	MD:3.18mm	ASTMD955	0.20到0.40	%
Modeling Shrinkage	Modeling Shrinkage	TD:3.18mm	ASTMD955	1.4到1.6	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Compressive Strength		ASTMD695	169	Mpa
Shearing Strength		ASTMD732	93.1	Mpa
Poisson Ratio		7.58	0.34
Nominal Tensile Strain at Break	--	ISO527-2/1A/5	2.7	%
Nominal Tensile Strain at Break	Nominal Tensile Strain at Break	--6	ASTMD638	2.7	%
Tensile Strength	Yield5	ASTMD638	158	Mpa
	Tensile Strength	Yield	ISO527-2/1A/5	165	Mpa
	Tensile Strength	Tensile Strength	--	ASTMD638	158	Mpa
Tensile Modulus	--5	ASTMD638	10500	Mpa
Tensile Modulus	Tensile Modulus	--	ISO527-2/1A/1	11400	Mpa
Flexural Modulus	--	ISO178	10700	Mpa
Flexural Modulus	Flexural Modulus	--	ASTMD790	10300	Mpa
Flexural Strength	--	ASTMD790	271	Mpa
	Flexural Strength	--	ISO178	246	Mpa
	Flexural Strength	Flexural Strength	Yield	ASTMD790	261	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,Annealed	ASTMD648	315	°C
Specific Heat	50°C	DSC	1300	J/kg/°C
Specific Heat	Specific Heat	200°C	DSC	1730	J/kg/°C
Thermal Conductivity		ASTME1530	0.29	W/m/K
Glass Transition Temperature		ASTMD3418	150	°C
Linear thermal expansion coefficient	MD：-50to50°C	ASTME831	1.7E-05	cm/cm/°C
Peak Melting Temperature		ASTMD3418	340	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	3.00mm	ASTMD149	17	KV/mm
Surface Resistivity		ASTMD257	>1.9E+17	ohms
Dielectric Constant	60Hz	ASTMD150	3.44
	Dielectric Constant	1kHz	ASTMD150	3.44
	Dielectric Constant	Dielectric Constant	1MHz	ASTMD150	3.41
Volume Resistivity		ASTMD257	1.9E+17	ohms·cm
Dissipation Factor?	60Hz	ASTMD150	1E-03
	Dissipation Factor?	1kHz	ASTMD150	1E-03
	Dissipation Factor?	Dissipation Factor?	1MHz	ASTMD150	3E-03

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Melt Viscosity	400°C,1000sec^-1	ASTMD3835	850	Pa·s

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	--	ISO180	56	kJ/m²
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	--	ASTMD4812	960	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTMD785	100
Shore Hardness	Shore D,1sec	ASTMD2240	91

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	20.3mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.