MS ACRYSTEX® PM-600 TAIWAN CHIMEI

Unit Price:
$2529 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
38.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate		ASTM D1238/ISO 1133	1.5	g/10min
Melt Mass-Flow Rate	Melt Mass-Flow Rate		ASTM D1238/ISO 1133	8.0	g/10min

Physical Properties	Test Condition	Test Method	Test Result	Unit
Transmittance	1/8"	ASTM D-1003	91

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Bending elasticity	1/4"，2.8mm/min	ASTM D-790	33000	kg/cm3
parent Hardness		ASTM D-785	M-85
Tensile Elongation	1/8"，6mm/min	ASTM D-638	8	%
Tensile strength	1/8"，6mm/min	ASTM D-638	700	kg/cm2
Tensile Elongation?(Break)		ASTM D638/ISO 527	5	%
Tensile Strength		ASTM D638/ISO 527	690	kg/cm²(MPa)[Lb/in²]
Flexural Modulus		ASTM D790/ISO 178	32000	kg/cm²(MPa)[Lb/in²]
Flexural Strength		ASTM D790/ISO 178	1000	kg/cm²(MPa)[Lb/in²]
Flexural Strength	Flexural Strength	1/4"，2.8mm/min	ASTM D-790	1050	kg/cm2
Izod Impact Strength	1/4"，23℃	ASTM D-256	1.7	kg.cm/cm
Izod notch impact strength		ASTM D256/ISO 179	1.8	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Burning Rate		UL94	1/16'HB
Deflection Temperature Under Load?		ASTM D648/ISO 75	89	℃（℉）
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1/4"，120℃/hr	ASTM D-648	89	°C
Vicat Softening Temperature	1/8"，50℃/hr	ASTM D-1525	105	°C

Physical	Test Condition	Test Method	Test Result	Unit
Melt index	200℃，5Kg	ASTM D-1238	1.5	g/10min

Other performance	Test Condition	Test Method	Test Result	Unit
Viscosity	1/8"	ASTM D-1003	0.4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.