Technical Data Sheet
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | MPa | ISO 527-2 | 13000 |
Charpy Unnotched Impact Strength | -30°C | kJ/m² | ISO 179/1eU | |
Charpy Unnotched Impact Strength | 23°C | kJ/m² | ISO 179/1eU | |
Tensile Stress | Break | MPa | ISO 527-2 | 185 |
Tensile Strain | Break | % | ISO 527-2 | 2.5 |
Charpy Notched Impact Strength | -30°C | kJ/m² | ISO 179/1eA | |
Charpy Notched Impact Strength | 23°C | kJ/m² | ISO 179/1eA | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa,Unannealed | °C | ISO 75-2/B | 250 |
Deflection Temperature Under Load? | 1.8 MPa,Unannealed | °C | ISO 75-2/A | 235 |
Coefficient of Linear Thermal Expansion | Flow | cm/cm/°C | ISO 11359-2 | 0.000025 |
Coefficient of Linear Thermal Expansion | Transverse | cm/cm/°C | ISO 11359-2 | 0.000040 |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ohms | IEC 60093 | |
Volume Resistivity | | ohm·cm | IEC 60093 | |
Comparative Tracking Index | | V | IEC 60112 | 250 |
Dielectric Strength | | kV/mm | IEC 60243-1 | 33 |
Dissipation Factor? | 100HZ | | IEC 60250 | 0.0030 |
Dissipation Factor? | 1E+6HZ | | IEC 60250 | 0.013 |
Relative Permittivity | 100HZ | | IEC 60250 | 3.70 |
Relative Permittivity | 1E+6HZ | | IEC 60250 | |
Other | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.50 mm | | IEC 60695-11-10, -20 | HB |
Flame Rating | 0.750 mm | | IEC 60695-11-10, -20 | HB |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | | g/cm³ | ISO 1183 | 1.63 |
Moisture Absorption | Saturation, 23°C | % | ISO 62 | 0.45 |
Moisture Absorption | Equilibrium, 23°C, 50% RH | % | ISO 62 | 0.18 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.