Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 230°C/2.16 kg | ISO 1133 | 34.0 | cm3/10min |
Density | | ISO 1183 | 1.11 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO 527-2 | 40.0 | Mpa |
Tensile Stress | Break | ISO 527-2 | 19.0 | Mpa |
Tensile Stress | 5.0% Strain | ISO 527-2 | 2.00 | Mpa |
Tensile Stress | 10% Strain | ISO 527-2 | 3.40 | Mpa |
Tensile Stress | 50% Strain | ISO 527-2 | 6.20 | Mpa |
Tensile Stress | 100% Strain | ISO 527-2 | 7.00 | Mpa |
Tensile Strain | Break | ISO 527-2 | > 300 | % |
Nominal Tensile Strain at Break | | ISO 527-2 | > 50 800 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | ISO 11357-3 | 195 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 无断裂 | |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 无断裂 | |
Notched Izod Impact Strength | -20°C | ISO 180/1A | 无断裂 | |
Notched Izod Impact Strength | 23°C | ISO 180/1A | 无断裂 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D, 3 sec | ISO 868 | 30 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.