PA6T Ultramid® TKR4355G7 BASF GERMANY

Unit Price:
$8784 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	4.3 到 5.3	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.80 到 1.2	%
Modeling Shrinkage	Across Flow	ISO 294-4	1.0	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	0.30	%
Apparent Density			0.70	g/cm³
Viscosity number	96% H2SO4	ISO 307	130	cm³/g
Modeling Shrinkage			0.35	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Creep Modulus	1000 hr	ISO 899-1	--	Mpa
Tensile Stress	Break	ISO 527-2	210	Mpa
Tensile Strain	Break	ISO 527-2	3.0	%
Tensile Modulus		ISO 527-2	12000	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	245	°C
Specific Heat			1300	J/kg/°C
Thermal Conductivity		DIN 52612	0.28	W/m/K
Linear thermal expansion coefficient	Flow : 23 to 55°C	ISO 11359-2	1.5E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	ISO 11359-2	5.0E-5 到 6.0E-5	cm/cm/°C
Melting temperature		ISO 11357-3	295	°C
Maximum Service Temperature (short cycle operation)			270	°C
Temperature Index	-- 5	IEC 60216	160	°C
Temperature Index	Temperature Index	-- 6	IEC 60216	135	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC 60243-1	33	KV/mm
Dissipation Factor?	1 MHz	IEC 60250	0.020
Relative Permittivity	1 MHz	IEC 60250	4.20
Comparative Tracking Index	Solution A	IEC 60112	600	V
Surface Resistivity		IEC 60093	--	ohms
Volume Resistivity		IEC 60093	1.0E+15	ohms·cm

Injection	Test Result	Unit
Residence Time	< 5.0	min
Screw Speed	< 18	m/min
Drying Temperature	110	°C
Suggested Max Moisture	0.15	%
Processing (Melt) Temp	310 到 330	°C
Mold Temperature	80 到 120	°C
Drying Time	8.0	hr
Rear Temperature	300	°C
Middle Temperature	310	°C
Front Temperature	320	°C
Nozzle Temperature	320	°C
Hopper Temperature	80	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	100	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Polymer Abbreviation			PA6T/6-GF35
Flammability level	1.6 mm	IEC 60695-11-10, -20	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.