Material Description
Technical Data Sheet
Material Description
- Material Properties:Mineral reinforcement Thermal stability
- Application Areas:Gear Engineering accessories Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1060 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eA | DAM｜4.2 | kJ/m² |
| -30℃ | ISO 179/1eA | 50%RH｜4 | kJ/m² | |
| 23℃ | ISO 179/1eA | DAM｜4.2 | kJ/m² | |
| 23℃ | ISO 179/1eA | 50%RH｜8 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30℃ | ISO 179/1eU | DAM｜NB | kJ/m² |
| -30℃ | ISO 179/1eU | 50%RH｜NB | kJ/m² | |
| 23℃ | ISO 179/1eU | DAM｜NB | kJ/m² | |
| 23℃ | ISO 179/1eU | 50%RH｜NB | kJ/m² | |
| IZOD Notch Impact Strength | -30℃ | ISO 180/1A | DAM｜4.9 | kJ/m² |
| -30℃ | ISO 180/1A | 50%RH｜4.3 | kJ/m² | |
| 23℃ | ISO 180/1A | DAM｜4 | kJ/m² | |
| 23℃ | ISO 180/1A | 50%RH｜6 | kJ/m² | |
| Tensile Modulus | 1mm/min | ISO 527-1/2 | DAM｜2400 | Mpa |
| 1mm/min | ISO 527-1/2 | 50%RH｜1550 | Mpa | |
| Tensile Strength | ASTM D412/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D412/ISO 527 | 4.5 | % | |
| Flexural Modulus | ASTM D790/ISO 178 | 2150 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Stress (Yield) | 50mm/min | ISO 527-1/2 | DAM｜4.3 | % |
| 50mm/min | ISO 527-1/2 | 50%RH｜19 | % | |
| Tensile Stress (Yield) | ISO 527-1/2 | DAM｜62 | Mpa | |
| ISO 527-1/2 | 50%RH｜52 | Mpa | ||
| Tensile Strain (Break) | 50mm/min | ISO 527-1/2 | DAM｜35 | % |
| 50mm/min | ISO 527-1/2 | 50%RH｜＞50 | % | |
| Izod notch impact strength | ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 10℃/min | ISO 3146C | DAM｜218 | °C |
| 10℃/min | ISO 3146C | 50%RH｜- | °C | |
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 62 | ℃（℉） | |
| Vicat Softening Temperature | 20N | ISO 306 | DAM｜181 | °C |
| 20N | ISO 306 | 50%RH｜- | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Constant | 0.45MPa | ISO 75-1/2 | 135 | °C |
| 1.80MPa | ISO 75-1/2 | DAM｜62 | °C | |
| 1.80MPa | ISO 75-1/2 | 50%RH｜- | °C | |
| Coefficient of Linear Thermal Expansion (Flow) | ASTM E-831 | DAM｜1.2 | 10-4/℃ | |
| ASTM E-831 | 50%RH｜- | 10-4/℃ | ||
| Coefficient of Linear Thermal Expansion (Flow) | ASTM D-831 | DAM｜1.2 | 10-4/℃ | |
| ASTM D-831 | 50%RH｜- | 10-4/℃ |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold Temperature | 50-90 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.