Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flow | | ASTMD955 | 0.20到0.60 | % |
-- | | ISO294-4 | 0.20到0.60 | % |
Moisture Absorption | Saturation,23°C | ASTMD570,ISO62 | 0.10 | % |
Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 6.0 | g/10min |
Melt Volume flow Rate | 200°C/5.0kg | ISO1133 | 6.00 | cm3/10min |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 65.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Field, 23°C | | ASTMD638 | 23.4 | Mpa |
Field, 23°C | | ISO527-2 | 28.0 | Mpa |
fracture | | ASTMD638 | 70 | % |
Break,23℃ | | ISO527-2 | 120 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
0.45MPa Annealed | | ISO75-2/B | 78.0 | °C |
1.8MPa, Unannealed | | ISO75-2/B | 86.1 | °C |
1.8MPa, Unannealed | | ISO75-2/A | 67.0 | °C |
-- | | ASTMD15251 | 93.9 | °C |
-- | | ISO306/B50 | 60.0 | °C |
Maximum Service Temperature | | | 250 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Gardner Impact | | ASTMD5420 | 19.2 | J |
23°C | | ASTMD256 | 590 | J/m |
23°C | | ISO180/A | 15 | kJ/m² |
Notched Izod impact strength | | ISO180 | 200 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 无断裂 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness (R-Scale) | | ASTMD785 | 62 | |
R-Scale | | ISO2039-2 | 62 | |
Ball Indentation Hardness | | ISO2039-1 | 35.0 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
--2 | | ASTMD542 | 1.570 | |
-- | | ISO489 | 1.560 | |
Transmittance | 550nm | ASTMD1003 | 91.0 | % |
Haze | | ASTMD1003 | 2.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.