MBS TP-801 DENKA JAPAN
190
- Unit Price:
- $2428 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 71.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent
- Application Areas:Home appliance components Household appliances Plastic toy Stationery Washing machine Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | 2mm | 0.3-0.5 | % | |
| Haze | 2mm | ASTM D-1003 | 2.5 | % |
| Transmittance | 2mm | ASTM D-1003 | 91 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ASTM D-790 | 2180 | Mpa | |
| Tensile Strength | ASTM D-638 | 42 | Mpa | |
| Rockwell Hardness | ASTM D-785 | 34 | M | |
| Flexural Strength | ASTM D-790 | 69 | Mpa | |
| Izod Impact Strength | 1/4〃带Notched | ASTM D-256 | 105 | J/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability | UL 94 | HB | ||
| Deflection Temperature Under Load? | 6.4mm,1.82MPa | ASTM D-648 | 72 | °C |
| Vicat Softening Temperature | 50N | ASTM D-1525 | 86 | °C |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 200℃×5N | ASTM D-1238 | 5.5 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.