Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 1.5 | % |
| Modeling Shrinkage | 流量 | ISO 294-4 | 1.2 | % |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.76 | % |
| Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 1.4 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield | ISO 527-2 | 23.0 | Mpa |
| Tensile Strain | Yield | ISO 527-2 | 22 | % |
| Nominal Tensile Strain at Break | | ISO 527-2 | > 50 | % |
| Abrasion Resistance | | ISO 4649 | 41.0 | mm³ |
| Tensile Modulus | | ISO 527-2 | 414 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO 306/B50 | 129 | °C |
| Melting Temperature | | ISO 11357-3 | 172 | °C |
| Extrusion | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 70 到 80 | °C |
| Drying Time | | | 5.0 到 7.0 | hr |
| Melt Temperature | | | 220 到 250 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 70 到 80 | °C |
| Processing (Melt) Temp | | | 230 到 290 | °C |
| Mold Temperature | | | 25 到 60 | °C |
| Drying Time | | | 5.0 到 7.0 | hr |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | -- | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | -- | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D, 15 sec | ISO 7619-1 | 61 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.