Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | % | 0.50 | -- |
| Modeling Shrinkage | MD | % | 0.10 | -- |
| Moisture Absorption | Saturation,23°C | % | 0.80 | -- |
| Moisture Absorption | Equilibrium,23°C,50%RH | % | 0.40 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break | MPa | 155 | |
| Tensile Strain | Break | % | 5.0 | 6.0 |
| Tensile Modulus | | MPa | 12000 | 11500 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | °C | 165 | -- |
| Deflection Temperature Under Load? | 8.0MPa,Unannealed | °C | 125 | -- |
| Linear thermal expansion coefficient | MD | cm/cm/°C | 1.5E-05 | -- |
| Linear thermal expansion coefficient | TD | cm/cm/°C | 1.2E-04 | -- |
| Continuous Use Temperature | --3 | °C | 90.0到120 | -- |
| Continuous Use Temperature | --4 | °C | 150 | -- |
| Melting Temperature | | °C | 178 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | kV/mm | -- | |
| Comparative Tracking Index | | V | -- | 600 |
| Surface Resistivity | | ohms | -- | 1E+12 |
| Volume Resistivity | | ohms·cm | -- | 1E+13 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | kJ/m² | 90 | |
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 90 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | | MPa | -- | 155 |
| Shore Hardness | Shore D,15sec | | -- | 82 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 0.8mm | | HB | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.