PA12 UBESTA 3030JI5L UBE JAPAN
144
- Unit Price:
- $15435 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Good flexibility High impact resistance heat-resisting Toughening
- Application Areas:Pipe fittings Automotive sector Pipe fittings
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.01 | kg·cm/cm(J/M)ft·lb/in | |
| Modeling Shrinkage | ASTM D955 | 0.7/1.4 | % | |
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 4 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | ISO 1133 | 4 | g/10min | |
| Modeling Shrinkage | ISO 294-4 | 0.7/1.4 | % | |
| TD | ISO294-4 | 1.4 | % | |
| MD | ISO294-4 | 0.70 | % | |
| Moisture Absorption | ISO 62 | 0.6 | % | |
| 23°C,24hr | ISO62 | 0.60 | % | |
| Melt Mass-Flow Rate | 235°C/2.16kg | ISO1133 | 4.0 | g/10min |
| Melting Temperature | ISO 11357-3 | 173 | °C |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO178 | 19.0 | Mpa | |
| Shore Hardness | ISO 868 | 67 | D | |
| Charpy Notched Impact Strength | -，23℃ | ISO 179/1eA | 115P | KJ/m |
| -，-40℃ | ISO 179/1eA | 4C | KJ/m | |
| Tensile Stress | Yield | ISO527-2 | 26.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 24 | % |
| Break | ISO527-2 | 200 | % | |
| Tensile Strength(Yield) | ISO 527-1/-2 | 26 | Mpa | |
| Tensile Elongation?(Break) | ASTM D412/ISO 527 | ＞200 | % | |
| Tensile Strength | ASTM D412/ISO 527 | 26 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | Break | ISO 527-1/-2 | ＞200 | % |
| Rockwell Hardness | ISO 2039-2 | 51 | R | |
| ASTM D785 | 51 | |||
| Flexural Modulus | ASTM D412/ISO 527 | 400 | kg/cm²(MPa)[Lb/in²] | |
| ISO 178 | 400 | Mpa | ||
| ISO178 | 400 | Mpa | ||
| Flexural Strength | ISO 178 | 19 | Mpa | |
| ASTM D790/ISO 178 | 19 | kg/cm²(MPa)[Lb/in²] |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 91 | ℃（℉） | |
| ASTM D648/ISO 75 | 45 | ℃（℉） | ||
| -，0.45Mpa | ISO 75-2 | 91 | °C | |
| -，1.8Mpa | ISO 75-2 | 45 | °C | |
| 0.45MPa,Unannealed | ISO75-2/B | 91.0 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 45.0 | °C | |
| Melting Temperature | 173 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 1.7 | mm/mm.℃ | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.7E-04 | cm/cm/°C |
| Melting temperature (DSC) | ISO3146 | 173 | °C | |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | 1.7 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | ASTM D257/IEC 60093 | 1012 | Ω.cm | |
| IEC60093 | 1E+12 | ohms·cm | ||
| IEC 60093 | 10 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Sale | ISO2039-2 | 51 | |
| Shore Hardness | Shore D | ISO868 | 67 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.