PBT NOVADURAN™ 5820G30 M MITSUBISHI ENGINEERING JAPAN
96
- Unit Price:
- $4235 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength
- Application Areas:Electronic and Electrical Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Across Flow : 2.00 mm | 内部方法 | 0.70 | % |
| 流量 : 2.00 mm | 内部方法 | 0.30 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.070 | % |
| Melt Volume flow Rate | 250°C/5.0 kg | ISO 1133 | 24.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO 178 | 9900 | Mpa | |
| Flexural Stress | ISO 178 | 190 | Mpa | |
| Tensile Stress | Break | ISO 527-2/5 | 134 | Mpa |
| Tensile Strain | Break | ISO 527-2/5 | 2.0 | % |
| Tensile Modulus | ISO 527-2/1 | 10600 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Annealed | ISO 75-2/B | 212 | °C |
| 1.8 MPa, Annealed | ISO 75-2/A | 178 | °C | |
| Linear thermal expansion coefficient | Flow : -30 to 35°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C |
| Flow : -30 to 120°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C | |
| Flow : 35 to 120°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C | |
| Across Flow : -30 to 35°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| Across Flow : -30 to 120°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Across Flow : 35 to 120°C | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 224 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 1.00 mm | IEC 60243-1 | 33 | KV/mm |
| 2.00 mm | IEC 60243-1 | 30 | KV/mm | |
| Surface Resistivity | IEC 60093 | 6.0E+15 | ohms | |
| Dielectric Constant | 1 MHz | IEC 60250 | 3.30 | |
| Volume Resistivity | IEC 60093 | 1.0E+14 | ohms·cm | |
| Dissipation Factor? | 1 MHz | IEC 60250 | 0.017 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Injection Pressure | 20.0 到 150 | Mpa | ||
| Injection Rate | 中等偏快 | |||
| Drying time - Hot air dryer | 120 | °C | ||
| Drying time - Hot air dryer | 5.0 到 8.0 | hr | ||
| Rear Temperature | 240 | °C | ||
| Middle Temperature | 245 | °C | ||
| Front Temperature | 255 | °C | ||
| Nozzle Temperature | 255 | °C | ||
| Screw Speed | 80 到 120 | rpm | ||
| Mold Temperature | 80 到 100 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179 | 38 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.