PBT VALOX™ 420SE0-11001 SABIC INNOVATIVE SHANGHAI

Unit Price:
$4142 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced dimensional stability High rigidity high strength heat-resisting
Application Areas:Lawn equipment Electrical field Electrical appliances Electronic field Electronic display Engine hood parts Textile application Industrial applications Nursing supplies Household goods Architectural application Automotive interior parts Automotive External Parts Petroleum Applications Outdoor applications sporting goods Natural gas supplies Medical supplies Garden equipment Lighting fixtures Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow 2	内部方法	0.10 到 0.50	%
	Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.50 到 0.70	%
		Modeling Shrinkage	Across Flow 2	内部方法	0.40 到 0.80	%
		Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.50 到 1.0	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.090	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.070	%
Specific Volume		ASTM D792	0.610	cm³/g
Outdoor Suitability		UL 746C	f2
Melt Mass-Flow Rate	250°C/5.0 kg	ASTM D1238	42	g/10 min
Melt Volume flow Rate	250°C/5.0 kg	ISO 1133	29.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	--	ISO 178	180	Mpa
Flexural Stress	Flexural Stress	Break, 50.0 mm Span 5	ASTM D790	186	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	内部方法	22.0	mg
Tensile Modulus	-- 3	ASTM D638	12000	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	10000	Mpa
Tensile Elongation	Yield 4	ASTM D638	2.0	%
	Tensile Elongation	Yield	ISO 527-2/5	1.9	%
		Tensile Elongation	Break 4	ASTM D638	2.0	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/5	1.9	%
Flexural Modulus	50.0 mm Span 5	ASTM D790	9800	Mpa
Flexural Modulus	Flexural Modulus	-- 6	ISO 178	9500	Mpa
Tensile Strength	Yield 4	ASTM D638	120	Mpa
	Tensile Strength	Yield	ISO 527-2/5	120	Mpa
		Tensile Strength	Break 4	ASTM D638	120	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/5	120	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152510, ISO 306/B50, ISO 306/B120	200	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/A50	220	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	2.5E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	2.5E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	8.9E-5	cm/cm/°C
			Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	8.9E-5	cm/cm/°C
			Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	1.2E-4	cm/cm/°C
Thermal Conductivity		ISO 8302	0.25	W/m/K
RTI		UL 746	140	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	212	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	220	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	200	°C
			Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	195	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	200	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	--	IEC 60112	175	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	125	V
High Voltage Arc Tracking Rate		UL 746	PLC 4
High Amp Arc Ignition		UL 746	PLC 0
Arc Resistance		ASTM D495	PLC 6
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 2
Dielectric Strength	1.60 mm, in Oil	ASTM D149	24	KV/mm
	Dielectric Strength	3.20 mm, in Air	ASTM D149	19	KV/mm
		Dielectric Strength	0.800 mm, in Oil	IEC 60243-1	23	KV/mm
			Dielectric Strength	1.60 mm, in Oil	IEC 60243-1	22	KV/mm
			Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	IEC 60243-1	16	KV/mm
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Dielectric Constant	100 Hz	ASTM D150, IEC 60250	3.80
	Dielectric Constant	1 MHz	ASTM D150	3.70
		Dielectric Constant	50 Hz	IEC 60250	3.30
			Dielectric Constant	60 Hz	IEC 60250	3.30
			Dielectric Constant	Dielectric Constant	1 MHz	IEC 60250	3.30
Volume Resistivity		ASTM D257, IEC 60093	> 1.0E+15	ohms·cm
Dissipation Factor?	100 Hz	ASTM D150, IEC 60250	2.0E-3
	Dissipation Factor?	1 MHz	ASTM D150	0.020
		Dissipation Factor?	50 Hz	IEC 60250	1.0E-3
			Dissipation Factor?	60 Hz	IEC 60250	1.0E-3
			Dissipation Factor?	Dissipation Factor?	1 MHz	IEC 60250	0.010

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	255 到 275	°C
Mold Temperature	65 到 90	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 80	%
Rear Temperature	245 到 265	°C
Middle Temperature	250 到 270	°C
Front Temperature	255 到 275	°C
Nozzle Temperature	250 到 270	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	50 到 80	rpm
Vent Depth	0.025 到 0.038	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	5.00	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	50	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	50	kJ/m²
Unnotched Izod Impact Strength	23°C	ASTM D4812	620	J/m
	Unnotched Izod Impact Strength	-30°C 8	ISO 180/1U	45	kJ/m²
	Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 8	ISO 180/1U	45	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	119
Rockwell Hardness	Rockwell Hardness	R -Sale	ISO 2039-2	119
Ball Indentation Hardness	H 358/30	ISO 2039-1	118	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Oxygen Index		ISO 4589-2	32	%
Flame Rating	0.40 mm	UL 94	V-2
	Flame Rating	0.71 mm	UL 94	V-0
	Flame Rating	Flame Rating	2.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.