PBT Ultradur® B 4040 G10 BK BASF GERMANY
116
- Unit Price:
- $4740 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High gloss High mobility
- Application Areas:Household appliances Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.20 | % | |
| Water absorption rate | Saturation | ASTMD570 | 0.40 | % |
| Saturation,23°C | ISO62 | 0.40 | % | |
| Equilibrium,50%RH | ASTMD570 | 0.12 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt volume flow rate | 275°C/2.16kg | ISO1133 | 6.00 | cm3/10min |
| Viscosity value | 降低的粘度 | ISO1628 | 97.0 | ml/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | 23°C | ISO178 | 225 | Mpa |
| Tensile strength | Break,23°C | ASTMD638 | 140 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 155 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 1.5 | % |
| Tensile modulus | 23°C | ISO527-2 | 16500 | Mpa |
| elongation | Break,23°C | ASTMD638 | 1.5 | % |
| Bending modulus | 23°C | ASTMD790 | 13600 | Mpa |
| 23°C | ISO178 | 15000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 220 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 221 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 215 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Melting temperature (DSC) | ISO3146 | 223 | °C | |
| Linear coefficient of thermal expansion | MD | 2.5E-05 | cm/cm/°C | |
| Peak melting temperature | ASTMD3418 | 223 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| VolumeResistivity | 1.50mm | ASTMD257 | >1.0E+15 | ohms·cm |
| Dissipation factor | 1MHz | IEC60250 | 0.015 | |
| 100Hz | IEC60250 | 1.2E-03 | ||
| SurfaceResistivity | 1.50mm | ASTMD257 | 1E+13 | ohms |
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Dielectric constant | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 4.00 | ||
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 69 | kJ/m² |
| 23°C | ISO179 | 52 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.