Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:3.00mm2 | 内部方法 | 1.7 | % |
Modeling Shrinkage | MD:3.00mm4 | 内部方法 | 1.8 | % |
Modeling Shrinkage | TD: 3.00 mm | Internal Method | 1.7 | % |
Modeling Shrinkage | MD: 3.00 mm | Internal Method | 1.8 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2 | 55.0 | Mpa |
Tensile Stress | Yield, 23℃ | ISO 527-2 | 55.0 | Mpa |
Tensile Strain | Break, 23℃ | ISO 527-2 | 1.8 | % |
Tensile Strain | Break,23°C | ISO527-2 | 1.8 | % |
Charpy Notched Impact Strength | 23℃ | ISO 179 | 2.0 | kJ/m² |
Charpy Notched Impact Strength | 23℃ | ISO 179 | 20 | kJ/m² |
Flexural Stress | 23°C | ISO178 | 100 | Mpa |
Tensile Modulus | 23℃ | ISO 527-2 | 4600 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 4600 | Mpa |
Rockwell Hardness | M -Sale | ISO 2039-2 | 80 | |
Flexural Modulus | 23℃ | ISO 178 | 4300 | Mpa |
Flexural Modulus | 23°C | ISO178 | 4300 | Mpa |
Flexural Strength | 23℃ | ISO 178 | 100 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 150 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 75.0 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 150 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 75.0 | °C |
Flame Rating | | UL 94 | HB | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 20 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Sale,23°C | ISO2039-2 | 80 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.