PBT Ultradur® B4300K6 BASF GERMANY
91
- Unit Price:
- $3743 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Glass fiber reinforced
- Application Areas:electrical machinery Engineering accessories Shell printed circuit board
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent Density | 0.70 到 0.80 | g/cm³ | ||
| Melt Volume flow Rate | 250℃，2.16 kg 250℃/2.16 kg | ISO 1133 | 9 | cm3/10min |
| Viscosity Number | ISO 307 | 113 | cm³/g | |
| Moisture Absorption | Saturation，23℃ Saturation, 73°F | ISO 62 | 0.4 | % |
| Equilibrium，23℃，50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 0.2 | % | |
| Modeling Shrinkage | MD：自由的 free, longitudinal | 1.7 | % | |
| TD：自由的 free, transverse | 1.7 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Break Break | ISO 527-2 | 50 | Mpa |
| Tensile Modulus | ISO 527-2 | 4000 | Mpa | |
| Tensile Strain | Break Break | ISO 527-2 | 5 | % |
| Tensile Creep Modulus | 1000 hr 1000 hr 5 | ISO 899-1 | 2200 | Mpa |
| Ball Indentation Hardness | H358/30 | ISO 2039-1 | 165 | Mpa |
| Electrical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100 Hz 100 Hz | IEC 60250 | 3.8 | |
| 1 MHz 1 MHz | IEC 60250 | 3.8 | ||
| Dissipation Factor | 100 Hz 100 Hz | IEC 60250 | 0.0012 | |
| 1 MHz 1 MHz | IEC 60250 | 0.019 | ||
| Comparative Tracking Index | Solution A Solution A | IEC 60112 | 225 | V |
| Solution B Solution B | IEC 60112 | 150 | V | |
| Volume Resistivity | IEC 60093 | 10000000000000000 | ohms·cm | |
| Surface Resistivity | IEC 60093 | 10000000000000 | ohms |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C -30°C | ISO 179/1eU | 24 | kJ/m² |
| 23℃ 23°C | ISO 179/1eU | 35 | kJ/m² |
| 特殊值 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.75 mm 0.75 mm | HB | ||
| 1.6 mm 1.6 mm | HB |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting Temperature | ISO 11357-3 | 223 | °C | |
| Coefficient of Linear Thermal Expansion | MD：23~80℃ MD：23 to 80℃ | ISO 11359-2 | 7.0E-5 到 8.0E-5 | 1/℃ |
| Specific Heat | 1500 | J/kg/℃ | ||
| Thermal Conductivity | DIN 52612 | 0.27 | W/m/K | |
| Temperature Index | -- -- 6 6 | IEC 60216 | 120 | °C |
| Temperature Index | -- -- 7 7 | IEC 60216 | 130 | °C |
| Maximum Service Temperature | short cycle operation | 200 | °C | |
| Heat Deflection Temperature | 0.45 MPa，Unannealed 66 psi, Unannealed | ISO 75-2/B | 200 | °C |
| 1.8 MPa，Unannealed 264 psi, Unannealed | ISO 75-2/A | 95 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.