PBT DURANEX® 3316 ED3002 JAPAN POLYPLASTIC

216

Unit Price:
$5635 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced
Application Areas:Electrical applications Electronic and electrical
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.30to0.50	%
	Shrinkage rate	TD	ISO294-4	0.80to1.3	%
	Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.10to0.80	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.16	%
Melt volume flow rate	250°C/2.16kg	ISO1133	7.00	cm3/10min
Density/specific gravity		ASTMD792	1.66	g/cm³
Density/specific gravity	Density/specific gravity		ISO1183	1.66	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break,23°C	ASTMD638	134	Mpa
Bending stress	23°C	ISO178	200	Mpa
Tensile stress	Break	ISO527-2/1A/5	135	Mpa
Tensile strain	Break	ISO527-2/1A/5	2.5	%
Tensile modulus	23°C	ASTMD638	9650	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1A/1	10700	Mpa
elongation	Break,23°C	ASTMD638	2.5	%
Bending modulus	23°C	ISO178	10300	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	220	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTMD648	221	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	206	°C
			Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	208	°C
			Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	165	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	2.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	7.7E-05	cm/cm/°C
Vicat softening temperature		ISO306/B50	225	°C
Peak melting temperature		ASTMD3418	225	°C
Melting temperature 2		ISO11357-3	225	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	100Hz	IEC60250	3.60
Relative permittivity	Relative permittivity	1MHz	IEC60250	2.90
Leakage Trace Index		ASTMD3638	250	V
Leakage Trace Index	Leakage Trace Index		IEC60112	250	V
Dielectric strength 3		ASTMD149	20	KV/mm
Dissipation factor	1MHz	ASTMD150	0.020
	Dissipation factor	100Hz	IEC60250	3.3E-03
	Dissipation factor	Dissipation factor	1MHz	IEC60250	0.015
Dielectric strength		IEC60243-1	34	KV/mm
Surface resistivity		IEC60093	1E+15	ohms
Dielectric constant	1MHz	ASTMD150	3.50
Arc resistance		ASTMD495	106	sec
Volume resistivity		ASTMD257	2E+16	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	1E+15	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	42	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	59	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	8.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	8.5	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO180/1A	7.7	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ISO2039-2	89

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	UL94	5VA
Extreme Oxygen Index		ISO4589-2	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.