Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Electrical field Electronic field Industrial applications switch Shell
Color:--
Grade:Flame retardant grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Specific volume		ASTM D792	0.710	cm³/g
Melt flow rate	250°C/2.16 kg	ASTM D1238	8.6	g/10 min
Molten Volume Flow Rate (MVR)	250°C/2.16 kg	ISO 1133	8.00	cm3/10min
Shrinkage rate	Flow 2	内部方法	1.1 到 1.8	%
	Shrinkage rate	Flow : 0.750 to 2.30 mm	内部方法	0.90 到 1.6	%
		Shrinkage rate	Flow : 3.20 mm	内部方法	1.5 到 2.3	%
			Shrinkage rate	Flow : 2.30 to 4.60 mm	内部方法	1.5 到 2.3	%
				Shrinkage rate	Across Flow 2	内部方法	0.90 到 1.9	%
					Shrinkage rate	Across Flow : 0.750 to 2.30 mm	内部方法	1.0 到 1.7	%
					Shrinkage rate	Shrinkage rate	Across Flow : 2.30 to 4.60 mm	内部方法	1.6 到 2.4	%
Water absorption rate	Saturation, 23°C	ISO 62	0.36	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.080	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 3	ASTM D638	2820	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2800	Mpa
Tensile strength	Yield 4	ASTM D638	58.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	58.0	Mpa
		Tensile strength	Break 4	ASTM D638	52.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	40.0	Mpa
elongation	Yield 4	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	5.0	%
		elongation	Break 4	ASTM D638	18	%
		elongation	elongation	Break	ISO 527-2/50	18	%
Bending modulus	50.0 mm Span 5	ASTM D790	2620	Mpa
Bending modulus	Bending modulus	-- 6	ISO 178	2600	Mpa
Bending stress	-- 6, 7	ISO 178	90.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 5	ASTM D790	101	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	内部方法	19.0	mg

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	162	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Be	150	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	74.0	°C
			Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	71.0	°C
				Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Ae	60.0	°C
				Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	73.0	°C
Vicat softening temperature	--	ASTM D152511, ISO 306/B50, ISO 306/B120	170	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	212	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.9E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 60 to 138°C	ASTM E831	1.3E-4	cm/cm/°C
		Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	7.6E-5	cm/cm/°C
			Linear coefficient of thermal expansion	Flow : 23 to 60°C	ISO 11359-2	1.0E-4	cm/cm/°C
				Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.9E-5	cm/cm/°C
					Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.3E-5	cm/cm/°C
					Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 60°C	ISO 11359-2	1.0E-4	cm/cm/°C
thermal conductivity		ISO 8302	0.24	W/m/K
RTI Elec		UL 746	120	°C
RTI Imp		UL 746	120	°C
RTI		UL 746	140	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	1.60 mm, in Oil	ASTM D149	24	KV/mm
	Dielectric strength	3.20 mm, in Air	ASTM D149	18	KV/mm
		Dielectric strength	0.800 mm, in Oil	IEC 60243-1	35	KV/mm
			Dielectric strength	1.00 mm 12	IEC 60243-1	18	KV/mm
				Dielectric strength	1.60 mm, in Oil	IEC 60243-1	25	KV/mm
				Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Relative permittivity	50 Hz	IEC 60250	2.90
	Relative permittivity	60 Hz	IEC 60250	2.90
		Relative permittivity	100 Hz	IEC 60250	3.10
		Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.80
Dissipation factor	50 Hz	IEC 60250	1.0E-3
	Dissipation factor	60 Hz	IEC 60250	1.0E-3
		Dissipation factor	100 Hz	IEC 60250	2.0E-3
		Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.013
Arc resistance 13		ASTM D495	PLC 6
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 3
Leakage Trace Index	--	IEC 60112	175	V
Leakage Trace Index	Leakage Trace Index	Solution B	IEC 60112	100	V
High arc combustion index (HAI) 14		UL 746	PLC 0
High Voltage Arc Resistance Index (HVAR) (PLC)		UL 746	PLC 6
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 4
Hot wire ignition (HWI)		UL 746	PLC 2

injection	Test Result	Unit
drying temperature	120	°C
drying time	3.0 到 4.0	hr
Suggested maximum moisture content	0.020	%
Suggested injection volume	40 到 80	%
Temperature at the rear of the barrel	230 到 250	°C
Temperature in the middle of the barrel	240 到 255	°C
Temperature at the front of the material cylinder	245 到 260	°C
Spray nozzle temperature	240 到 255	°C
Processing (melt) temperature	245 到 260	°C
Mold temperature	50 到 75	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	50 到 100	rpm
Exhaust hole depth	0.013 到 0.025	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Simple supported beam without notch impact strength 8	-30°C	ISO 179/1eU	无断裂
Simple supported beam without notch impact strength 8	Simple supported beam without notch impact strength 8	23°C	ISO 179/1eU	无断裂
Non notched cantilever beam impact	23°C	ASTM D4812, ISO 180/1U	无断裂
Non notched cantilever beam impact	Non notched cantilever beam impact	-30°C 9	ISO 180/1U	无断裂
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	200	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R -Sale	ISO 2039-2	120
Ball pressure hardness	H 358/30	ISO 2039-1	105	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.71 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.