Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.35 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break | ISO527-2 | 108 | Mpa |
| Tensile Strain | Break | ISO527-2 | 2.5 | % |
| Flexural Stress | | ISO178 | 160 | Mpa |
| Tensile Modulus | | ASTM D638/ISO 527 | 7000 | kg/cm²(MPa)[Lb/in²] |
| Tensile Modulus | | ISO527-2 | 7000 | Mpa |
| Flexural Modulus | | ISO178 | 6200 | Mpa |
| Flexural Modulus | | ASTM D790/ISO 178 | 6200 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 160 | kg/cm²(MPa)[Lb/in²] |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | UL94 | HB | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 205 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 150 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Annealed | ISO75-2/A | 180 | °C |
| Melting Temperature | | ISO11357-3 | 225 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 50 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94,IEC60695-11-10,-20 | HB | |
| Burning Rate | 1.00mm | ISO3795 | 38 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| Odor | | VDA270 | 3.50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.