PBT Cristin® ST820 NC010 DUPONT USA

Unit Price:
$6800 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High impact resistance
Application Areas:Electronic and electrical
Color:--
Grade:Toughened grade

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	1220
Modeling Shrinkage	ASTM D955	1.8	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	0.12	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.8	%
	Modeling Shrinkage	MD2	ISO294-4	2.5	%
	Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.9	%
Moisture Absorption	Saturation,23°C,2.00mm	ISO62	0.31	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.12	%
MediumDensity			1.03	g/cm³
Ejection Temperature			170	°C
SpecificHeatCapacityofMelt			2100	J/kg/°C
ThermalConductivityofMelt			0.20	W/m/K

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	50.0	Mpa
Tensile Strength	23℃	MPa	ASTM D695	43
Tensile Elongation?(Break)	23℃	%	ASTM D638	150
Notched Izod Impact Strength		J/m	ASTM D256	117
Nominal Tensile Strain at Break		ISO527-2	>50	%
Unnotched Izod Impact Strength	-，-40℃	J/m	ASTM D256	No Break
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	-，23℃	J/m	ASTM D256	No Break
Tensile Stress	Yield	ISO527-2	38.0	Mpa
Tensile Strain	Yield	ISO527-2	7.0	%
Notched Impact Strength	-，-40℃	J/m	ASTM D256	117
Notched Impact Strength	Notched Impact Strength	-，23℃	J/m	ASTM D256	No Break
Tensile Elongation?(Break)		ASTM D638/ISO 527	150	%
Tensile Modulus		ASTM D638/ISO 527	1700	kg/cm²(MPa)[Lb/in²]
	Tensile Modulus		ISO527-2	1700	Mpa
	Tensile Modulus	Tensile Modulus	23℃	MPa	ASTM D638	1600
Tensile Strength	23℃	MPa	ASTM D638	37
Flexural Modulus	23℃	MPa	ASTM D790	1680
	Flexural Modulus		ISO178	1550	Mpa
	Flexural Modulus	Flexural Modulus		ASTM D790/ISO 178	1550	kg/cm²(MPa)[Lb/in²]
Flexural Strength		ASTM D790/ISO 178	50	kg/cm²(MPa)[Lb/in²]
Flexural Strength	Flexural Strength	23℃	MPa	ASTM D638	53

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Burning Rate		UL94	HB(0.8mm)
Deflection Temperature Under Load?		ASTM D648/ISO 75	100	℃（℉）
	Deflection Temperature Under Load?		ASTM D648/ISO 75	145	℃（℉）
		Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	100	°C
			Deflection Temperature Under Load?	0.45MPa,Annealed	ISO75-2/B	145	°C
				Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	50.0	°C
					Deflection Temperature Under Load?	-，66 psi， Unannealed	℃	ASTM D648
					Deflection Temperature Under Load?	Deflection Temperature Under Load?	-，264 psi，Unannealed	℃	ASTM D648	47
Melting Temperature		℃	DSC	225
Melting Temperature	Melting Temperature			225	℃（℉）
Vicat Softening Temperature		ASTM D1525/ISO R306	216	℃（℉）
Linear thermal expansion coefficient	MD	ISO11359-2	1.9E-04	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1.9E-04	cm/cm/°C
Coefficient of Linear Thermal Expansion	-，平行Flow	cm/cm/℃	ASTM E831	0.00019
Coefficient of Linear Thermal Expansion	Coefficient of Linear Thermal Expansion	-，垂直Flow	cm/cm/℃	ASTM E831	0.00019
Vicat Softening Temperature		ISO306/B50	125	°C
Melting Temperature		ISO11357-3	225	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC60243-1	27	KV/mm
Comparative Tracking Index		IEC60112	600	V
Dissipation Factor?	100Hz	IEC60250	0.020
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.019
Surface Resistivity		ASTM D257/IEC 60093	1.00E+15	Ω
Surface Resistivity	Surface Resistivity		IEC60093	1E+15	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Volume Resistivity	Volume Resistivity		ASTM D257/IEC 60093	>1E13	Ω.cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Notched Izod impact strength	-40°C	ISO180/1U	270	kJ/m²
	Notched Izod impact strength	-30°C	ISO180/1U	NoBreak
	Notched Izod impact strength	Notched Izod impact strength	23°C	ISO180/1U	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ISO2039-2	104

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
Oxygen Index		ISO4589-2	19	%
FMVSS Flammability		FMVSS302	B
Fogging-G-value	condensate	ISO6452	1E-04	g
Burning Rate	1.00mm	ISO3795	38	mm/min

Other performance	Test Condition	Test Method	Test Result	Unit
Oxygen Index		%	ASTM D2863	22

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.