Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1370 | |
Modeling Shrinkage | | ASTM D955 | 1.2 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Ejection Temperature | | | 170 | °C |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 140 | Mpa |
Tensile Stress | Break | ISO527-2 | 90.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 4.0 | % |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 4 | % |
Tensile Modulus | 0.00 mm, 23℃, Injection Molded | MPa | ISO 527-1, -2 | 4500 |
Tensile Modulus | | ISO527-2 | 4500 | Mpa |
Flexural Strength | 0.00 mm, 23 ℃, 0.0 % | MPa | ISO 178 | 140 |
Flexural Strength | | ASTM D790/ISO 178 | 140 | kg/cm²(MPa)[Lb/in²] |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | HB | |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 180 | ℃(℉) |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 180 | °C |
Melting Temperature | | | 225 | ℃(℉) |
Flame Rating | -,6.00 mm | | UL 94 | HB |
Flame Rating | -,3.00 mm | | UL 94 | HB |
Flame Rating | -,1.50 mm | | UL 94 | HB |
Melting Temperature | | ISO11357-3 | 225 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | | IEC60112 | 250 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 35 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 35 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
Oxygen Index | | ISO4589-2 | 20 | % |
FMVSS Flammability | | FMVSS302 | B | |
Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
Burning Rate | 1.00mm | ISO3795 | 36 | mm/min |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
EmissionofOrganicCompounds | | VDA277 | 72.0 | µgC/g |
Odor | | VDA270 | 3.00 | |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | % | ISO 4589-1, -2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.