PBT Cristin® SK602 NC010 DUPONT USA
129
- Unit Price:
- $3442 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 72.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 15% filler by weight
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.40 | % | |
| MDLength2(2.00mm) | ISO294-4 | 360 | mm | |
| Top out temperature | 170 | °C | ||
| Density/specific gravity | g/cm³ | ISO 1183 | ||
| ISO1183 | 1.41 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2 | 109 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.5 | % |
| Tensile modulus | 0.00 mm, 23 ℃, Injection Molded | MPa | ISO 527-1, -2 | |
| ISO527-2 | 5800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 200 | °C |
| Flame retardant grade | -，6.00 mm | UL 94 | HB | |
| -，3.00 mm | UL 94 | HB | ||
| -，1.50 mm | UL 94 | HB | ||
| Melting temperature 5 | ISO11357-3 | 225 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dissipation factor | 100Hz | IEC60250 | 7E-04 | |
| 1MHz | IEC60250 | 0.017 | ||
| Dielectric strength | IEC60243-1 | 35 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.70 | |
| 1MHz | IEC60250 | 3.60 | ||
| Leakage Trace Index | IEC60112 | 225 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 40 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 5.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Burning rate 4 | 1.00mm | ISO3795 | 30 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.