PBT Cristin® HR5330HF BK503 DUPONT USA
101
- Unit Price:
- $5800 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electronic and electrical
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.0 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.35 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| MediumDensity | 1.29 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1730 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.28 | W/m/K | ||
| FlowLength2 | 2.00mm | 350 | mm | |
| Stickiness number | ISO307 | 95.0 | cm³/g | |
| Density/specific gravity | ISO1183 | 1.50 | g/cm³ | |
| g/cm | ISO 1183 | 1.5 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Poisson's ratio 3 | ISO527 | 0.34 | ||
| Yield point tensile stress | 23℃ | MPa | ISO 527-1, -2 | 134 |
| Yield point tensile strain | 23℃ | % | ISO 527-1, -2 | |
| Charpy non notched impact strength | 23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | 75.1 |
| Charpy notch impact strength | -，-30 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 11.5 |
| -，23 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 14.9 | |
| Bending stress | ISO178 | 200 | Mpa | |
| Tensile stress | Break | ISO527-2 | 132 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.5 | % |
| Gap impact strength | -，-40 ℃, Type 1, Notch A | KJ/m | ISO 180 | 11.1 |
| -，23 ℃, Type 1, Notch A | KJ/m | ISO 180 | 16.3 | |
| Tensile modulus | 23℃ | MPa | ISO 527-1, -2 | 8500 |
| ISO527-2 | 8500 | Mpa | ||
| Bending modulus | 23℃ | MPa | ISO 178 | 7800 |
| ISO178 | 7700 | Mpa | ||
| bending strength | 23℃ | MPa | ISO 178 | 203 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 221 |
| -，1.80 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 207 | |
| 0.45MPa,Unannealed | ISO75-2/B | 221 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 207 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 2E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.5E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Vicat softening temperature | ISO306/B50 | 215 | °C | |
| Melting temperature 5 | ISO11357-3 | 225 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100Hz | IEC60250 | 2.5E-03 | |
| 1MHz | IEC60250 | 0.020 | ||
| 100Hz | ASTMD150 | 2.5E-03 | ||
| 1kHz | ASTMD150 | 7E-03 | ||
| 1MHz | ASTMD150 | 0.020 | ||
| Dielectric strength | -- | IEC60243-1 | 44 | KV/mm |
| 1.00mm5 | IEC60243-1 | 31 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.40 | |
| 1MHz | IEC60250 | 4.10 | ||
| Leakage Trace Index | IEC60112 | 450 | V | |
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 70 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 65 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 | kJ/m² |
| 23°C | ISO179/1eA | 13 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 11 | kJ/m² |
| 23°C | ISO180/1A | 14 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | HB | |
| Extreme Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Flammability level | 0.75mm | IEC60695-11-10,-20 | HB | |
| Burning rate 6 | 1.00mm | ISO3795 | 30 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.