PBT VALOX™ DR48-BK1066 SABIC INNOVATIVE SHANGHAI

190

Unit Price:
$3623 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Glass fiber reinforced
Application Areas:Lawn equipment Electrical field Electrical appliances Electronic field Electronic display Engine hood parts Non specific food Industrial applications Nursing supplies Architectural application Side track application Automotive interior parts Automotive External Parts Outdoor applications Medical supplies Garden equipment Lighting fixtures
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow : 1.50 to 3.20 mm	内部方法	0.40 到 0.60	%
	Shrinkage rate	Flow : 3.20 to 4.60 mm	内部方法	0.60 到 0.90	%
		Shrinkage rate	Across Flow : 1.50 to 3.20 mm	内部方法	0.50 到 0.80	%
		Shrinkage rate	Shrinkage rate	Across Flow : 3.20 to 4.60 mm	内部方法	0.80 到 1.1	%
Water absorption rate	24 hr	ASTM D570	0.070	%
Specific volume		ASTM D792	0.650	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending modulus	50.0 mm Span	ASTM D790	5200	Mpa
bending strength	Break, 50.0 mm Span	ASTM D790	140	Mpa
Tensile strength	Break	ASTM D638	93.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	140	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	120	°C
Linear coefficient of thermal expansion - flow	-40 to 40°C	ASTM E831	2.0E-5	cm/cm/°C
Linear coefficient of thermal expansion - flow	Linear coefficient of thermal expansion - flow	60 to 138°C	ASTM E831	2.0E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	210	°C
Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	182	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 3
Hot wire ignition (HWI)		UL 746	PLC 3
High arc combustion index (HAI) 5		UL 746	PLC 0
Dielectric constant	100 Hz	ASTM D150	3.60
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.40
Volume resistivity		ASTM D257	1.0E+15	ohms·cm
Dissipation factor	100 Hz	ASTM D150	2.0E-3
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.016
Dielectric strength	1.60 mm, in Oil	ASTM D149	25	KV/mm
Dielectric strength	Dielectric strength	3.20 mm, in Air	ASTM D149	19	KV/mm
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 4
Arc resistance 4		ASTM D495	PLC 6

injection	Test Result	Unit
drying temperature	120	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	250 到 265	°C
Mold temperature	65 到 90	°C
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 80	%
Temperature at the rear of the barrel	240 到 255	°C
Temperature in the middle of the barrel	245 到 260	°C
Temperature at the front of the material cylinder	250 到 265	°C
Spray nozzle temperature	245 到 260	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	50 到 80	rpm
Exhaust hole depth	0.025 到 0.038	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Non notched cantilever beam impact	23°C	ASTM D4812	500	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	118

flammability	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index		ASTM D2863	29	%
UL flame retardant rating	0.9 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.