PBT Cristin® LW9320 DUPONT USA

Unit Price:
$4286 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	0.70	%
	Modeling Shrinkage	MD	ISO294-4	0.40	%
		Modeling Shrinkage	-，Across Flow	%	ISO 294-4	0.65
		Modeling Shrinkage	Modeling Shrinkage	-，Flow	%	ISO 294-4
Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.30	%
MediumDensity			1.17	g/cm³
Ejection Temperature			170	°C
SpecificHeatCapacityofMelt			1900	J/kg/°C
ThermalConductivityofMelt			0.24	W/m/K
Viscosity number		ISO307	120	cm³/g
Melt Volume flow Rate	250°C/5.0kg	ISO1133	15.0	cm3/10min
Density / Specific Gravity		g/cm	ISO 1183	1.35
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.34	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23 ℃, Type 1, Edgewise	KJ/m	ISO 179	55
Charpy Notched Impact Strength	23 °C, Type 1, Edgewise, Notch A	KJ/m	ISO 179	8.5
Tensile Strain (Break)		%	ISO 527-1, -2	2.7
Tensile Stress (Break)	23℃	MPa	ISO 527-1, -2
Tensile Stress	Break	ISO527-2	120	Mpa
Tensile Strain	Break	ISO527-2	2.5	%
Tensile Modulus	23℃	MPa	ISO 527-1, -2	7400
Tensile Modulus	Tensile Modulus		ISO527-2	7500	Mpa
Flexural Modulus		ISO178	7000	Mpa
Flexural Modulus	Flexural Modulus	23℃	MPa	ISO 178	6100
Notched Impact Strength	-，-40 ℃, Type 1, Notch A	KJ/m	ISO 180
Notched Impact Strength	Notched Impact Strength	-，23 ℃, Type 1, Notch A	KJ/m	ISO 180

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Flame retardancy	-，0.750 mm		UL94	HB
	Flame retardancy	-，1.50 mm		UL94	HB
	Flame retardancy	Flame retardancy	-，3.00 mm		UL94	HB
Deflection Temperature Under Load?	1.80 Mpa，Unannealed	℃	ISO 75A-1, -2	180
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	175	°C
Linear thermal expansion coefficient	TD	ISO11359-2	1E-04	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	MD	ISO11359-2	3E-05	cm/cm/°C
Melting temperature		℃	ISO 3146
Melting Temperature		ISO11357-3	220	°C
Glass Transition Temperature		ISO11357-2	110	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		IEC60112	500	V

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	45	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	50	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	8.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	8.5	kJ/m²
Notched Izod Impact Strength	-40°C	ISO180/1A	7.0	kJ/m²
	Notched Izod Impact Strength	-30°C	ISO180/1A	7.0	kJ/m²
	Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	7.0	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.75mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
FMVSS Flammability		FMVSS302	B
Burning Rate	1.00mm	ISO3795	30	mm/min

Supplementary information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	130	µgC/g
Odor		VDA270	3.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.