PBT VALOX™ DR48-7001 SABIC INNOVATIVE NANSHA

Unit Price:
$3663 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 1.50 to 3.20 mm	内部方法	0.40 到 0.60	%
	Modeling Shrinkage	Flow : 3.20 to 4.60 mm	内部方法	0.60 到 0.90	%
		Modeling Shrinkage	Across Flow : 1.50 to 3.20 mm	内部方法	0.50 到 0.80	%
		Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 to 4.60 mm	内部方法	0.80 到 1.1	%
Moisture Absorption	24 hr	ASTM D570	0.070	%
Specific Volume		ASTM D792	0.650	cm³/g

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	50.0 mm Span	ASTM D790	5200	Mpa
Flexural Strength	Break, 50.0 mm Span	ASTM D790	140	Mpa
Tensile Strength	Break	ASTM D638	93.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Coefficient of Linear Thermal Expansion (Flow)	-40 to 40°C	ASTM E831	2.0E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion (Flow)	Coefficient of Linear Thermal Expansion (Flow)	60 to 138°C	ASTM E831	2.0E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	210	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	182	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过
RTI		UL 746	140	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	120	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	100 Hz	ASTM D150	2.0E-3
Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.016
Dielectric Strength	1.60 mm, in Oil	ASTM D149	25	KV/mm
Dielectric Strength	Dielectric Strength	3.20 mm, in Air	ASTM D149	19	KV/mm
Dielectric Constant	100 Hz	ASTM D150	3.60
Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.40
Volume Resistivity		ASTM D257	1.0E+15	ohms·cm
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 3
High Amp Arc Ignition		UL 746	PLC 0
High Voltage Arc Tracking Rate		UL 746	PLC 4
Arc Resistance		ASTM D495	PLC 6

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	250 到 265	°C
Mold Temperature	65 到 90	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 80	%
Rear Temperature	240 到 255	°C
Middle Temperature	245 到 260	°C
Front Temperature	250 到 265	°C
Nozzle Temperature	245 到 260	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	50 到 80	rpm
Vent Depth	0.025 到 0.038	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	500	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	118

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.9 mm	UL 94	V-0
Flame Rating	Flame Rating	3.0 mm	UL 94	5VA
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	3.0 mm 6	IEC 60695-2-12	960	°C
Oxygen Index		ASTM D2863	29	%
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	700	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	725	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.