PBT VALOX™ 420-1001 SABIC INNOVATIVE SHANGHAI

Unit Price:
$5657 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：--3	内部方法	0.30to0.50	%
	Modeling Shrinkage	TD：3.20mm	内部方法	0.50to1.0	%
		Modeling Shrinkage	TD：--2	内部方法	0.50to1.0	%
			Modeling Shrinkage	TD：--5	内部方法	0.60to0.90	%
				Modeling Shrinkage	TD：--3	内部方法	0.40to0.60	%
					Modeling Shrinkage	MD：--4	内部方法	0.50to0.80	%
						Modeling Shrinkage	MD：--2	内部方法	0.30to0.70	%
						Modeling Shrinkage	Modeling Shrinkage	MD：3.20mm	内部方法	0.30to0.80	%
Moisture Absorption	24hr	ASTMD570	0.090	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.080	%
Melt Mass-Flow Rate	250°C/2.16kg	ISO1133	17	g/10min
Melt Volume flow Rate	250°C/2.16kg	ISO1133	13.0	cm3/10min
Specific Volume		ASTMD792	0.660	cm³/g

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strain	Yield	ASTMD638	2.7	%
Tensile Strain	Tensile Strain	Break	ASTMD638	2.7	%
Flexural Modulus	50.0mmSpan	ASTMD790	7580	Mpa
Tensile Strength	Yield	ASTMD638	120	Mpa
Tensile Strength	Tensile Strength	Break	ASTMD638	120	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	195	Mpa
Flexural Strength	Flexural Strength	Break,50.0mmSpan	ASTMD790	190	Mpa
Flexural Modulus		ISO178	8500	Mpa
Taber Abrasion Resistance	1000Cycles,1000g,CS-17Wheel	ASTMD1044	19.0	mg
Tensile Stress	Yield	ISO527-2/5	125	Mpa
Tensile Stress	Tensile Stress	Break	ISO527-2/5	125	Mpa
Tensile Strain	Break	ISO527-2/5	2.0	%
Tensile Strain	Tensile Strain	Yield	ISO527-2/5	2.0	%
Tensile Modulus		ISO527-2/1	9300	Mpa
Flexural Modulus		ISO178	195	Mpa
Tensile Modulus		ASTMD638	9300	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	204	°C
Heat Deflection Temperature	Heat Deflection Temperature	0.45MPa,Unannealed,64.0mmSpan	ISO75-2/Bf	217	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,6.40mm	ASTMD648	216	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	203	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed,6.40mm	ASTMD648	207	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	220	°C
Linear thermal expansion coefficient	TD：-40to40°C	ISO11359-2	1.2E-04	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	2.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	MD：60to138°C	ASTME831	2.5E-05	cm/cm/°C
			Linear thermal expansion coefficient	MD：-40to40°C	ISO11359-2	2.5E-05	cm/cm/°C
			Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	1.2E-04	cm/cm/°C
RTIElec		UL746	140	°C
Evolution Calendar intelligent importer		UL746	140	°C
RTIStr		UL746	140	°C
Vicat Softening Temperature		ASTMD152514	215	°C
	Vicat Softening Temperature	--	ISO306/B120	215	°C
		Vicat Softening Temperature	--	ISO306/A50	223	°C
		Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	215	°C
Thermal Conductivity		ISO8302	0.19	W/m/K
Ball PressureTest	125°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	CTI	UL746	PLC0
Relative Permittivity	60Hz	IEC60250	3.10
	Relative Permittivity	50Hz	IEC60250	3.10
	Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.10
Comparative Tracking Index		IEC60112	300	V
Dissipation Factor?	100Hz	ASTMD150	2E-03
	Dissipation Factor?	1MHz	ASTMD150	0.020
		Dissipation Factor?	50Hz	IEC60250	1E-03
			Dissipation Factor?	60Hz	IEC60250	1E-03
				Dissipation Factor?	100Hz	IEC60250	1E-03
				Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.010
Dielectric Strength	1.00mm15	IEC60243-1	19	KV/mm
	Dielectric Strength	1.60mm,in Oil	ASTMD149	25	KV/mm
		Dielectric Strength	0.800mm,in Oil	IEC60243-1	28	KV/mm
			Dielectric Strength	3.20mm,in Oil	IEC60243-1	16	KV/mm
				Dielectric Strength	1.60mm,in Oil	IEC60243-1	24	KV/mm
				Dielectric Strength	Dielectric Strength	3.20mm,inAir	ASTMD149	19	KV/mm
Surface Resistivity		IEC60093	>1.0E+15	ohms
Dielectric Constant	100Hz	ASTMD150	3.80
Dielectric Constant	Dielectric Constant	1MHz	ASTMD150	3.70
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Volume Resistivity	Volume Resistivity		ASTMD257	>3.2E+16	ohms·cm
Arc Resistance		ASTMD495	PLC5
High Voltage Arc Tracking Rate	HVTR	UL746	PLC1

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	8.00	J
Charpy Unnotched Impact Strength	23°C	ISO179/1eU	45	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	45	kJ/m²
Charpy Notched Impact Strength	23°C	ISO179/1eA	5.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO179/1eA	5.0	kJ/m²
Unnotched Izod Impact Strength	23°C	ISO180/1U	45	kJ/m²
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	-30°C	ISO180/1U	45	kJ/m²
Notched Izod Impact Strength	23°C	ISO180/1A	8.0	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	-30°C	ISO180/1A	7.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTMD785	118
Rockwell Hardness	Rockwell Hardness	R-Scale	ISO2039-2	118
Ball Indentation Hardness	H358/30	ISO2039-1	122	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
Glow Wire Flammability Index	1.0mm	IEC60695-2-12	750	°C
Oxygen Index		ASTMD2863	19	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
Filler Content		ASTMD229	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.