Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | -，Across Flow | % | ISO 294-4 | 0.60 |
| Modeling Shrinkage | TD | ISO294-4 | 0.60 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.30 | % |
| Modeling Shrinkage | -，Flow | % | ISO 294-4 | 0.30 |
| Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.25 | % |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 1.0 | % |
| Melt Mass-Flow Rate | | ISO1133 | 13 | g/10min |
| MediumDensity | | | 1.27 | g/cm³ |
| Ejection Temperature | | | 170 | °C |
| SpecificHeatCapacityofMelt | | | 1790 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.28 | W/m/K |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Density / Specific Gravity | | g/cm | ISO 1183 | 1.42 |
| Density / Specific Gravity | | ISO1183 | 1.42 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | 55 |
| Charpy Notched Impact Strength | 23 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | |
| Unnotched Izod Impact Strength | -，-40 ℃, Type 1 | KJ/m | ISO 180 | 55 |
| Unnotched Izod Impact Strength | -，23 ℃, Type 1 | KJ/m | ISO 180 | |
| Tensile Strain (Break) | | % | ISO 527-1, -2 | 2.3 |
| Tensile Stress (Break) | 23℃ | MPa | ISO 527-1, -2 | |
| Tensile Stress | Break | ISO527-2 | 135 | Mpa |
| Tensile Strain | Break | ISO527-2 | 2.3 | % |
| Tensile Modulus | 23℃ | MPa | ISO 527-1, -2 | 9800 |
| Tensile Modulus | | ISO527-2 | 9800 | Mpa |
| Flexural Modulus | | ISO178 | 8400 | Mpa |
| Flexural Modulus | 23℃ | MPa | ISO 178 | 8400 |
| Notched Impact Strength | -，-40 °C, Type 1, Notch A | KJ/m | ISO 180 | |
| Notched Impact Strength | -，23 °C, Type 1, Notch A | KJ/m | ISO 180 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame retardancy | -，0.750 mm | | UL 94 | HB |
| Flame retardancy | -，1.50 mm | | UL 94 | HB |
| Flame retardancy | -，3.00 mm | | UL 94 | HB |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 185 | °C |
| Deflection Temperature Under Load? | 1.80 Mpa，Unannealed | ℃ | ISO 75A-1, -2 | 185 |
| Melting temperature | | ℃ | ISO 3146 | |
| Melting Temperature | | ISO11357-3 | 225 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | | IEC60112 | 550 | V |
| Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -40°C | ISO179/1eU | 50 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 55 | kJ/m² |
| Notched Izod impact strength | -40°C | ISO180/1U | 45 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO180/1U | 45 | kJ/m² |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 9.0 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 9.0 | kJ/m² |
| Notched Izod Impact Strength | -40°C | ISO180/1A | 7.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 7.0 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| FMVSS Flammability | | FMVSS302 | B | |
| Burning Rate | 1.00mm | ISO3795 | 28 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.