PBT Toraycon® 1101G-30 TORAY JAPAN

205

Unit Price:
$3867 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant High impact resistance
Application Areas:Electrical field Electronic field Automotive sector
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.55
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	0.07	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.00mm1	内部方法	1.0	%
Shrinkage rate	Shrinkage rate	MD:3.00mm2	内部方法	0.30	%
Water absorption rate	23°C,24hr	ISO62	0.070	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	23°C	ISO527-2	145	Mpa
Tensile strain	Break,23°C	ISO527-2	2.5	%
Bending stress	23°C	ISO178	220	Mpa
Friction coefficient vs. Metal4		SuzukiMethod	0.150
elongation at break		ASTM D638/ISO 527	5	%
Tensile modulus	23°C	ISO527-2	10200	Mpa
tensile strength		ASTM D638/ISO 527	145	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M91
Bending modulus		ASTM D790/ISO 178	8800	kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus	23°C	ISO178	9600	Mpa
bending strength		ASTM D790/ISO 178	195	kg/cm²(MPa)[Lb/in²]
Friction coefficient 3			0.19
IZOD notch impact strength		ASTM D256/ISO 179	90	kg·cm/cm(J/M)ft·lb/in
	IZOD notch impact strength		ASTM D256/ISO 179	75	kg·cm/cm(J/M)ft·lb/in
		IZOD notch impact strength		ASTM D256/ISO 179	65	kg·cm/cm(J/M)ft·lb/in
		IZOD notch impact strength	IZOD notch impact strength		ASTM D256/ISO 179	35	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	HB
Hot deformation temperature		ASTM D648/ISO 75	217	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	2.0x10^-5	mm/mm.℃
0.45MPa, unannealed		ISO75-2/B	220	°C
1.8MPa, unannealed		ISO75-2/A	213	°C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO11359-2	4.1E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the anti leakage trace index	CTI	UL746	PLC2
Dissipation factor 6	23°C,50Hz	IEC60250	2E-03
Dissipation factor 6	Dissipation factor 6	23°C,1MHz	IEC60250	0.020
Arc resistance 7		IEC60950	120	sec
Dielectric constant 5	23°C,50Hz	IEC60250	3.70
Dielectric constant 5	Dielectric constant 5	23°C,1kHz	IEC60250	4.20
Dielectric strength		IEC60243-1	36	KV/mm
Volume resistivity		IEC60093	5E+16	ohms·cm
Volume resistivity	Volume resistivity		ASTM D257/IEC 60093	2.5x10^14	Ω.cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	45	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale,23°C	ISO2039-2	90

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.794mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength8	250°C,1.00mm	内部方法	9.60	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.