PBT Crastin® SK605 DUPONT TAIWAN
93
- Unit Price:
- $3259 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 65MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% by weight ratio) 30% filler by weight Good strength Good hardness (glass fibe 30% by weight ratio) 30% filler by weight Good strength Good hardness (glass fibe
- Application Areas:Electronic and electrical Industrial applications household electrical appl Structural components switch Automotive Applications Shell Spool
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.35 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| Melt Mass-Flow Rate | ISO1133 | 10 | g/10min | |
| MediumDensity | 1.36 | g/cm³ | ||
| Ejection Temperature | 170 | °C | ||
| SpecificHeatCapacityofMelt | 1730 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.28 | W/m/K | ||
| Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 7.00 | cm3/10min |
| Viscosity number | ISO307 | 100 | cm³/g | |
| Density / Specific Gravity | ASTM D792 | 1.53 | ||
| ISO1183 | 1.53 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Creep Modulus | 1hr | ISO899-1 | 9000 | Mpa |
| Tensile Strength | 5 mm/min, 3.20 mm, 23 ℃ | MPa | ASTM D695 | 202 |
| Tensile Elongation?(Break) | 23℃ | % | ASTM D638 | 2.6 |
| Notched Izod Impact Strength | J/m | ASTM D256 | 101 | |
| Unnotched Izod Impact Strength | -，-40℃ | J/m | ASTM D256 | 1120 |
| -，23℃ | J/m | ASTM D256 | 998 | |
| Notched Impact Strength | -，-40℃ | J/m | ASTM D256 | 101 |
| -，23℃ | J/m | ASTM D256 | 112 | |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 6600 | Mpa |
| Flexural Stress | ISO178 | 200 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 140 | Mpa |
| Tensile Strain | Break | ISO527-2 | 2.7 | % |
| Tensile Modulus | 23℃ | MPa | ASTM D638 | 10000 |
| ISO527-2 | 10000 | Mpa | ||
| Tensile Strength | 23℃ | MPa | ASTM D638 | 140 |
| Flexural Modulus | ISO178 | 9000 | Mpa | |
| 23℃ | MPa | ASTM D790 | 8970 | |
| Flexural Strength | 23℃ | MPa | ASTM D790 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| -，0.45Mpa,Unannealed | ℃ | ASTM D648 | ||
| -，1.8Mpa,Unannealed | ℃ | ASTM D648 | 205 | |
| Melting Temperature | ℃ | 225 | ||
| Flame Rating | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| Linear thermal expansion coefficient | TD | ISO11359-2 | 9E-05 | cm/cm/°C |
| MD | ISO11359-2 | 3E-05 | cm/cm/°C | |
| Vicat Softening Temperature | ISO306/B50 | 215 | °C | |
| Melting Temperature | ISO11357-3 | 224 | °C | |
| Coefficient of Linear Thermal Expansion | 平行Flow ，73 to 130°F (23 to 55℃) | cm/cm/℃ | ASTM E831 | 0.000030 |
| 垂直Flow ，73 to 130°F (23 to 55℃) | cm/cm/℃ | ASTM E831 | 0.000090 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 38 | KV/mm | |
| Dissipation Factor? | 100Hz | IEC60250 | 7.5E-04 | |
| 1MHz | IEC60250 | 0.018 | ||
| Relative Permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.80 | ||
| Comparative Tracking Index | IEC60112 | 400 | V | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -40°C | ISO179/1eU | 75 | kJ/m² |
| -30°C | ISO179/1eU | 75 | kJ/m² | |
| 23°C | ISO179/1eU | 70 | kJ/m² | |
| Notched Izod impact strength | -40°C | ISO180/1U | 55 | kJ/m² |
| -30°C | ISO180/1U | 55 | kJ/m² | |
| 23°C | ISO180/1U | 60 | kJ/m² | |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 10 | kJ/m² |
| -30°C | ISO179/1eA | 11 | kJ/m² | |
| 23°C | ISO179/1eA | 10 | kJ/m² | |
| Notched Izod Impact Strength | -40°C | ISO180/1A | 10 | kJ/m² |
| -30°C | ISO180/1A | 10 | kJ/m² | |
| 23°C | ISO180/1A | 11 | kJ/m² |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | % | ASTM D2863 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS Flammability | FMVSS302 | B | ||
| Burning Rate | 1.00mm | ISO3795 | 41 | mm/min |
| Fogging-F-value | refraction | ISO6452 | 99 | % |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.