PBT Cristin® SK605 DUPONT USA
127
- Unit Price:
- $3617 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 90MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% by weight ratio) 30% filler by weight Good strength Good hardness (glass fibe
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.35 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | ISO1133 | 10 | g/10min | |
| MediumDensity | 1.36 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1730 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.28 | W/m/K | ||
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 7.00 | cm3/10min |
| Stickiness number | ISO307 | 100 | cm³/g | |
| Density/specific gravity | ASTM D792 | 1.53 | ||
| ISO1183 | 1.53 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 9000 | Mpa |
| compressive strength | 5 mm/min, 3.20 mm, 23 ℃ | MPa | ASTM D695 | 202 |
| Across Flow | 23℃ | % | ASTM D638 | 2.6 |
| Low temperature notch impact strength | J/m | ASTM D256 | 101 | |
| Non notched impact strength | -，-40℃ | J/m | ASTM D256 | 1120 |
| -，23℃ | J/m | ASTM D256 | 998 | |
| Gap impact strength | -，-40℃ | J/m | ASTM D256 | 101 |
| -，23℃ | J/m | ASTM D256 | 112 | |
| Tensile creep modulus | 1000hr | ISO899-1 | 6600 | Mpa |
| Bending stress | ISO178 | 200 | Mpa | |
| Tensile stress | Break | ISO527-2 | 140 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.7 | % |
| Tensile modulus | 23℃ | MPa | ASTM D638 | 10000 |
| ISO527-2 | 10000 | Mpa | ||
| tensile strength | 23℃ | MPa | ASTM D638 | 140 |
| Bending modulus | ISO178 | 9000 | Mpa | |
| 23℃ | MPa | ASTM D790 | 8970 | |
| bending strength | 23℃ | MPa | ASTM D790 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| -，0.45Mpa,Unannealed | ℃ | ASTM D648 | ||
| -，1.8Mpa,Unannealed | ℃ | ASTM D648 | 205 | |
| melting point | ℃ | 225 | ||
| Flame retardant grade | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 9E-05 | cm/cm/°C |
| MD | ISO11359-2 | 3E-05 | cm/cm/°C | |
| Vicat softening temperature | ISO306/B50 | 215 | °C | |
| Melting temperature 2 | ISO11357-3 | 224 | °C | |
| Linear coefficient of thermal expansion | 平行Flow ，73 to 130°F (23 to 55℃) | cm/cm/℃ | ASTM E831 | 0.000030 |
| 垂直Flow ，73 to 130°F (23 to 55℃) | cm/cm/℃ | ASTM E831 | 0.000090 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC60243-1 | 38 | KV/mm | |
| Dissipation factor | 100Hz | IEC60250 | 7.5E-04 | |
| 1MHz | IEC60250 | 0.018 | ||
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.80 | ||
| Leakage Trace Index | IEC60112 | 400 | V | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO179/1eU | 75 | kJ/m² |
| -30°C | ISO179/1eU | 75 | kJ/m² | |
| 23°C | ISO179/1eU | 70 | kJ/m² | |
| Unscented Izod impact strength | -40°C | ISO180/1U | 55 | kJ/m² |
| -30°C | ISO180/1U | 55 | kJ/m² | |
| 23°C | ISO180/1U | 60 | kJ/m² | |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 10 | kJ/m² |
| -30°C | ISO179/1eA | 11 | kJ/m² | |
| 23°C | ISO179/1eA | 10 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 10 | kJ/m² |
| -30°C | ISO180/1A | 10 | kJ/m² | |
| 23°C | ISO180/1A | 11 | kJ/m² |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | % | ASTM D2863 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 3 | 1.00mm | ISO3795 | 41 | mm/min |
| Fogging-F-value | refraction | ISO6452 | 99 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.