PPO NORYL™ SE1GFN2 - 780 SABIC INNOVATIVE SHANGHAI
99
- Unit Price:
- $5419 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan High mobility Glass fiber reinforced
- Application Areas:Electrical applications Automotive interior parts
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 280°C/5.0 kg | ASTM D1238 | 3.5 | g/10 min |
| Molten Volume Flow Rate (MVR) | 280°C/5.0 kg | ISO 1133 | 3.00 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.20 到 0.50 | % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.11 | % |
| 24 hr, 23°C 2 | ISO 62 | 0.040 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | -- 6, 7 | ISO 178 | 150 | Mpa |
| Yield, 50.0 mm Span 5 | ASTM D790 | 140 | Mpa | |
| Tensile modulus | -- 3 | ASTM D638 | 7100 | Mpa |
| -- | ISO 527-2/1 | 6400 | Mpa | |
| elongation | Break 4 | ASTM D638 | 3.0 | % |
| Break | ISO 527-2/50 | 2.5 | % | |
| Bending modulus | 50.0 mm Span 5 | ASTM D790 | 5500 | Mpa |
| -- 6 | ISO 178 | 5600 | Mpa | |
| Tensile strength | Break 4 | ASTM D638 | 120 | Mpa |
| Break | ISO 527-2/50 | 100 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ASTM D15259, ISO 306/B509 | 142 | °C |
| -- | ISO 306/B120 | 144 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 2.5E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 3.0E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 7.5E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 142 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 134 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 133 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 1.60 mm, in Oil | ASTM D149 | 26 | KV/mm |
| 1.50 mm, in Oil | IEC 60243-1 | 26 | KV/mm | |
| Surface resistivity | ASTM D257, IEC 60093 | 1.3E+17 | ohms | |
| Dielectric constant | 1 MHz | ASTM D150 | 2.93 | |
| 1 MHz | IEC 60250 | 2.90 | ||
| Volume resistivity | ASTM D257, IEC 60093 | 2.0E+16 | ohms·cm | |
| Dissipation factor | 1 MHz | ASTM D150, IEC 60250 | 3.4E-3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 110 到 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 300 到 325 | °C | ||
| Mold temperature | 80 到 110 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 265 到 315 | °C | ||
| Temperature in the middle of the barrel | 275 到 320 | °C | ||
| Temperature at the front of the material cylinder | 290 到 325 | °C | ||
| Spray nozzle temperature | 300 到 325 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 520 | J/m |
| -30°C 8 | ISO 180/1U | 27 | kJ/m² | |
| 23°C 8 | ISO 180/1U | 28 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 18.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.