PPO NORYL™ GFN30F-701S SABIC INNOVATIVE SHANGHAI
137
- Unit Price:
- $4925 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Low warpage Low Specific Gravity
- Application Areas:Shower Water pump impeller Water meter component Water treatment equipment Water filter Faucet
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10to0.40 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Melt mass flow rate | 300°C/5.0kg | ASTMD1238 | 8.7 | g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 7.82 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2 | 117 | Mpa |
| Tensile strain | Break | ISO527-2 | 1.8 | % |
| Tensile modulus | ISO527-2/1 | 8740 | Mpa | |
| Bending modulus | ISO178 | 8710 | Mpa | |
| 100mmSpan5 | ASTMD790 | 7170 | Mpa | |
| 50.0mmSpan4 | ASTMD790 | 8000 | Mpa | |
| bending strength | Yield,100mmSpan5 | ASTMD790 | 162 | Mpa |
| Yield,50.0mmSpan4 | ASTMD790 | 180 | Mpa | |
| Bending stress | ISO178 | 183 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 9150 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 116 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 8 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 137 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 143 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 142 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 158 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 137 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C | |
| RTIElec | UL746 | 90.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 147 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 3.1E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 6.2E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| High arc combustion index | HAI | UL746 | PLC4 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| 60Hz | ASTMD150 | 9E-04 | ||
| Dielectric constant | 50Hz | ASTMD150 | 2.93 | |
| 60Hz | ASTMD150 | 2.93 | ||
| Hot wire ignition | HWI | UL746 | PLC4 | |
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 22 | KV/mm |
| Arc resistance 9 | ASTMD495 | PLC7 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 7 | 23°C | ISO180/1A | 12 | kJ/m² |
| -30°C | ISO180/1A | 12 | kJ/m² | |
| Unscented Izod Impact Strength 7 | 23°C | ISO180/1U | 32 | kJ/m² |
| -30°C | ISO180/1U | 36 | kJ/m² | |
| Simple supported beam without notch impact strength 6 | 23°C | ISO179/1eU | 39 | kJ/m² |
| -30°C | ISO179/1eU | 47 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L-Sale | ASTMD785 | 108 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Extreme Oxygen Index | ASTMD2863 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.