Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD2 | 内部方法 | 1.1到1.3 | % |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ISO178 | 4000 | Mpa |
| Flexural Stress | | ISO178 | 110 | Mpa |
| Tensile Stress | Break | ISO527-2/5 | 65.0 | Mpa |
| Tensile Strain | Break | ISO527-2/5 | 4.0 | % |
| Tensile Modulus | | ISO527-2/1 | 4200 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | -- | ISO306/B50 | 195 | °C |
| Vicat Softening Temperature | -- | ISO306/B120 | 200 | °C |
| Linear thermal expansion coefficient | MD:23to60°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:23to60°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 185 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | 内部方法 | 1.0E+3到1.0E+4 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 35 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 40 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 3.5 | kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 35 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 40 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 4.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 125 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.