PPO NORYL™ N1250 BK1066 SABIC INNOVATIVE SHANGHAI
172
- Unit Price:
- $4043 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan High mobility Glass fiber reinforced
- Application Areas:Electrical applications Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 300°C/5.0 kg | ASTM D1238 | 28 | g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 2680 | Mpa | |
| Elongation rate 3 | Yield | ASTM D638 | 4.6 | % |
| Break | ASTM D638 | 25 | % | |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2680 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 113 | Mpa |
| Tensile strength 3 | Yield | ASTM D638 | 75.0 | Mpa |
| Break | ASTM D638 | 64.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ASTM D15255 | 137 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 6.1E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 6.8E-5 | cm/cm/°C | |
| RTI | UL 746 | 115 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI Elec | UL 746 | 110 | °C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 131 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 133 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 116 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 122 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance 6 | ASTM D495 | PLC 6 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| High arc combustion index (HAI) 7 | UL 746 | PLC 0 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 0 | ||
| High Voltage Arc Resistance Index (HVAR) (PLC) | UL 746 | PLC 4 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 245 到 295 | °C | ||
| Temperature in the middle of the barrel | 255 到 300 | °C | ||
| Temperature at the front of the material cylinder | 265 到 305 | °C | ||
| Spray nozzle temperature | 275 到 305 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm | ||
| drying temperature | 105 到 110 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 275 到 305 | °C | ||
| Mold temperature | 70 到 100 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 40.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
| 0.76 mm | UL 94 | V-0 | ||
| 2.5 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.