PPO NORYL GTX™ GTX910 SABIC INNOVATIVE US
80
- Unit Price:
- $5138 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 130°C, 1hr | ASTM D955 | 1.6 到 1.8 | % |
| Flow : 3.20 mm | 内部方法 | 1.1 到 1.3 | % | |
| Across Flow : 3.20 mm | 内部方法 | 1.0 到 1.2 | % | |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.50 | % |
| Equilibrium, 50% RH | ASTM D570 | 1.0 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | ASTM D638 | 60 | % |
| Flexural Modulus | 100 mm Span | ASTM D790 | 2240 | Mpa |
| Flexural Strength | Yield, 100 mm Span | ASTM D790 | 95.0 | Mpa |
| Tensile Strength | Yield | ASTM D638 | 59.0 | Mpa |
| Break | ASTM D638 | 55.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTM D15254 | 232 | °C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 193 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 143 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 95°C | ASTM E831 | 9.0E-5 | cm/cm/°C |
| Flow : 60 to 138°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 9.0E-5 | cm/cm/°C | |
| Across Flow : 60 to 138°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| RTI | UL 746 | 50.0 | °C | |
| RTI Imp | UL 746 | 50.0 | °C | |
| RTI Elec | UL 746 | 50.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High Amp Arc Ignition | UL 746 | PLC 0 | ||
| High Voltage Arc Tracking Rate | UL 746 | PLC 4 | ||
| Arc Resistance | ASTM D495 | PLC 7 | ||
| Comparative Tracking Index | UL 746 | PLC 1 | ||
| Hot-wire Ignition | UL 746 | PLC 3 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 30 到 50 | % | ||
| Rear Temperature | 265 到 305 | °C | ||
| Middle Temperature | 270 到 305 | °C | ||
| Front Temperature | 275 到 305 | °C | ||
| Nozzle Temperature | 280 到 305 | °C | ||
| Back Pressure | 0.300 到 1.40 | Mpa | ||
| Screw Speed | 20 到 100 | rpm | ||
| Vent Depth | 0.013 到 0.038 | mm | ||
| Drying Temperature | 95 到 105 | °C | ||
| Suggested Max Moisture | 0.070 | % | ||
| Processing (Melt) Temp | 280 到 305 | °C | ||
| Mold Temperature | 75 到 120 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | -30°C, Energy at Peak | ASTM D3763 | 39.0 | J |
| 23°C, Energy at Peak | ASTM D3763 | 50.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTM D785 | 116 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.