Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow 2	内部方法	0.50 到 0.70	%
Moisture Absorption	24 hr	ASTM D570	0.060	%
Outdoor Suitability		UL 746C	f2

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	100 mm Span	ASTM D790	2640	Mpa
Flexural Strength	Yield, 100 mm Span	ASTM D790	111	Mpa
Tensile Elongation	Yield	ASTM D638	9.5	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	18	%
Tensile Strength	Yield	ASTM D638	75.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	55.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	133	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	122	°C
RTI		UL 746	110	°C
RTI Imp		UL 746	105	°C
RTI Elec		UL 746	110	°C
Vicat Softening Temperature		ASTM D15255	150	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		ASTM D257	> 1.0E+16	ohms
Dielectric Constant	60 Hz	ASTM D150	2.57
	Dielectric Constant	50 kHz	ASTM D150	2.57
	Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	2.49
Volume Resistivity		ASTM D257	2.0E+16	ohms·cm
Dissipation Factor?	50 Hz	ASTM D150	5.2E-3
	Dissipation Factor?	60 Hz	ASTM D150	5.2E-3
	Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	2.6E-3
Dielectric Strength	3.20 mm, in Oil	ASTM D149	19	KV/mm
High Voltage Arc Tracking Rate		UL 746	PLC 4
Arc Resistance		ASTM D495	PLC 6
Comparative Tracking Index		UL 746	PLC 2
High Amp Arc Ignition		UL 746	PLC 0
Hot-wire Ignition		UL 746	PLC 0

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	30 到 70	%
Rear Temperature	245 到 295	°C
Middle Temperature	255 到 300	°C
Front Temperature	265 到 305	°C
Nozzle Temperature	275 到 305	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	20 到 100	rpm
Vent Depth	0.038 到 0.051	mm
Drying Temperature	105 到 110	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	275 到 305	°C
Mold Temperature	70 到 100	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	1100	J/m
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	42.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.76 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.