PPO NORYL GTX™ GTX974 SABIC INNOVATIVE US
103
- Unit Price:
- $5940 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Conductive
- Application Areas:Household appliances Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:3.20mm | 内部方法 | 1.1到1.4 | % |
| MD2 | 内部方法 | 1.6到2.0 | % | |
| MD:3.20mm | 内部方法 | 1.4到1.7 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 3.5 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.2 | % | |
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 13 | g/10min |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 13.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Yield4 | ASTMD638 | 65.0 | Mpa |
| Yield | ISO527-2/50 | 65.0 | Mpa | |
| Break4 | ASTMD638 | 55.0 | Mpa | |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| Flexural Stress | --6,7 | ISO178 | 90.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 95.0 | Mpa | |
| Tensile Modulus | --3 | ASTMD638 | 2300 | Mpa |
| -- | ISO527-2/1 | 2400 | Mpa | |
| Tensile Elongation | Yield4 | ASTMD638 | 5.0 | % |
| Yield | ISO527-2/50 | 4.5 | % | |
| Break4 | ASTMD638 | 60 | % | |
| Break | ISO527-2/50 | 25 | % | |
| Flexural Modulus | 50.0mmSpan5 | ASTMD790 | 2350 | Mpa |
| --6 | ISO178 | 2200 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 190 | °C |
| 0.45MPa,Unannealed,100mmSpan10 | ISO75-2/Be | 190 | °C | |
| Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD:23to60°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 8.5E-05 | cm/cm/°C | |
| TD:23to60°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Vicat Softening Temperature | -- | ASTM D-596 | 205 | °C |
| -- | ISO306/A50 | 250 | °C | |
| -- | ISO306/B50 | 200 | °C | |
| Thermal Conductivity | ISO8302 | 0.23 | W/m/K | |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 60.0 | J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 20 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 85.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.