PPO NORYL™ SE1GFN1-701 SABIC INNOVATIVE SHANGHAI
197
- Unit Price:
- $4242 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 28MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced Flame retardant High mobility High temperature resistan
- Application Areas:Electronic communication Electronic communication Household appliances Household appliances Automotive interior parts Above water Sports Equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.070 | % |
| Equilibrium, 23°C | ASTM D570 | 0.22 | % | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.30 到 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Break | ASTM D638 | 74.0 | Mpa |
| elongation | Break | ASTM D638 | 5.0 | % |
| Bending modulus | 50.0 mm Span | ASTM D790 | 3990 | Mpa |
| bending strength | Break, 50.0 mm Span | ASTM D790 | 119 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | UL 746 | 110 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI Elec | UL 746 | 110 | °C | |
| Vicat softening temperature | ASTM D15254 | 147 | °C | |
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 131 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 1 | ||
| High arc combustion index (HAI) 5 | UL 746 | PLC 2 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | ||
| Dielectric constant | 60 Hz | ASTM D150 | 3.00 | |
| 50 kHz | ASTM D150 | 3.00 | ||
| 1 MHz | ASTM D150 | 3.00 | ||
| Volume resistivity | ASTM D257 | 1.0E+15 | ohms·cm | |
| Dissipation factor | 50 Hz | ASTM D150 | 1.7E-3 | |
| 60 Hz | ASTM D150 | 1.7E-3 | ||
| 1 MHz | ASTM D150 | 1.6E-3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 105 到 110 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 280 到 310 | °C | ||
| Mold temperature | 75 到 105 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 250 到 300 | °C | ||
| Temperature in the middle of the barrel | 260 到 305 | °C | ||
| Temperature at the front of the material cylinder | 270 到 310 | °C | ||
| Spray nozzle temperature | 280 到 310 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L -Sale | ASTM D785 | 104 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTM D2863 | 34 | % | |
| UL flame retardant rating | 1.5 mm | UL 94 | V-1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.