PPO NORYL™ SE1GFN2-701 SABIC INNOVATIVE SHANGHAI
174
- Unit Price:
- $5061 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced
- Application Areas:Electronic communication Electronic communication
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 280°C/5.0 kg | ASTM D1238 | 3.5 | g/10 min |
| Melt Volume flow Rate | 280°C/5.0 kg | ISO 1133 | 3.00 | cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.20 到 0.50 | % |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.11 | % |
| 24 hr, 23°C 2 | ISO 62 | 0.040 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | -- 6, 7 | ISO 178 | 150 | Mpa |
| Yield, 50.0 mm Span 5 | ASTM D790 | 140 | Mpa | |
| Tensile Modulus | -- 3 | ASTM D638 | 7100 | Mpa |
| -- | ISO 527-2/1 | 6400 | Mpa | |
| Tensile Elongation | Break 4 | ASTM D638 | 3.0 | % |
| Break | ISO 527-2/50 | 2.5 | % | |
| Flexural Modulus | 50.0 mm Span 5 | ASTM D790 | 5500 | Mpa |
| -- 6 | ISO 178 | 5600 | Mpa | |
| Tensile Strength | Break 4 | ASTM D638 | 120 | Mpa |
| Break | ISO 527-2/50 | 100 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTM D15259, ISO 306/B509 | 142 | °C |
| -- | ISO 306/B120 | 144 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831 | 2.5E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 3.0E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 7.5E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 142 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 134 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 133 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 26 | KV/mm |
| 1.50 mm, in Oil | IEC 60243-1 | 26 | KV/mm | |
| Surface Resistivity | ASTM D257, IEC 60093 | 1.3E+17 | ohms | |
| Dielectric Constant | 1 MHz | ASTM D150 | 2.93 | |
| 1 MHz | IEC 60250 | 2.90 | ||
| Volume Resistivity | ASTM D257, IEC 60093 | 2.0E+16 | ohms·cm | |
| Dissipation Factor? | 1 MHz | ASTM D150, IEC 60250 | 3.4E-3 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 110 到 120 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 300 到 325 | °C | ||
| Mold Temperature | 80 到 110 | °C | ||
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 30 到 70 | % | ||
| Rear Temperature | 265 到 315 | °C | ||
| Middle Temperature | 275 到 320 | °C | ||
| Front Temperature | 290 到 325 | °C | ||
| Nozzle Temperature | 300 到 325 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 20 到 100 | rpm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 520 | J/m |
| -30°C 8 | ISO 180/1U | 27 | kJ/m² | |
| 23°C 8 | ISO 180/1U | 28 | kJ/m² | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 18.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.5 mm | UL 94 | V-1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.