Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.85 | % |
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 0.20 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Yield,23°C | ISO527-2 | 150 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 2.5 | % |
| Bending modulus | 23°C | ISO178 | 10000 | Mpa |
| Taber abraser | 1000Cycles | ISO9352 | 50.0 | mg |
| shear strength | 23°C | JISK7214 | 68.0 | Mpa |
| Bending stress | 23°C | ISO178 | 225 | Mpa |
| Friction coefficient 4 | | | 0.25 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 255 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 3.3E-05 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 278 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | | IEC60243-1 | 26 | KV/mm |
| Dielectric constant 6 | 23°C,1MHz | IEC60250 | 3.80 | |
| Dissipation factor 5 | 23°C,1MHz | IEC60250 | 2E-03 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 60 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 114 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| BarFlowLength6 | 320°C,1.00mm | 内部方法 | 150 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.