Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:3.00mm2 | 内部方法 | 0.50 | % |
| Modeling Shrinkage | MD:3.00mm4 | 内部方法 | 0.25 | % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.020 | % |
| Density / Specific Gravity | 23°C | ISO1183 | 1.99 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield,23°C | ISO527-2 | 105 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 0.90 | % |
| Flexural Modulus | 23°C | ISO178 | 19500 | Mpa |
| Taber Abrasion Resistance | 1000Cycles | ISO9352 | 70.0 | mg |
| Shearing Strength | 23°C | JISK7214 | 60.0 | Mpa |
| Flexural Stress | 23°C | ISO178 | 210 | Mpa |
| Coefficient of Friction | | | 0.30 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.9E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 278 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Dielectric Strength | | IEC60243-1 | 21 | KV/mm |
| Dielectric Constant | 23°C,1MHz | IEC60250 | 5.30 | |
| Dissipation Factor | 23°C,1MHz | IEC60250 | 2E-03 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 17 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 7.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ISO2039-2 | 122 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.72mm | UL94 | V-0 | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| BarFlowLength6 | 320°C,1.00mm | 内部方法 | 8.00 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.