PPS Susteel® GS-40 TOSOH JAPAN

127

Unit Price:
$9847 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:enhance Glass fiber reinforced
Application Areas:Fiber grade
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Method	Test Result	Unit
density	ASTM D792/ISO 1183	1.64
Molding shrinkage rate	ASTM D955	0.3~0.8	%
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.02	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	0.80	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.30	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO62	<0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield	ISO527-2	176	Mpa
Tensile strain	Break	ISO527-2	1.5	%
Bending modulus		ISO178	14700	Mpa
Bending stress		ISO178	275	Mpa
Tensile Weld Strength		内部方法	60.0	Mpa
Elongation rate		ASTM D-638	1.7	%
tensile strength		ASTM D-638	172	Mpa
Charpy impact strength	有Notched	ASTM D-256	74	J/m
Charpy impact strength	Charpy impact strength	Unnotched	ASTM D-256	541	J/m
Rockwell hardness		ASTM D-785	122
bending strength		ASTM D-790	275	Mpa
Bending modulus		ASTM D-790	15	GPa
elongation at break		ASTM D638/ISO 527	1.5	%
tensile strength		ASTM D638/ISO 527	176	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	14700	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	275	kg/cm²(MPa)[Lb/in²]
IZOD notch impact strength		ASTM D256/ISO 179	82	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion		自定标准	2.2
Flame retardancy		UL 94	V-0
Hot deformation temperature	1.82MPa	ASTM D-648	＞260	°C
Hot deformation temperature	Hot deformation temperature		ASTM D648/ISO 75	260	℃（℉）
melting point			285	℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	>260	°C
Melting temperature		内部方法	285	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	1E+17	ohms·cm
Dielectric strength		IEC60243-1	16	KV/mm
Dielectric constant	1MHz	IEC60250	3.90
Dissipation factor	1MHz	IEC60250	1.4E-03
Compared to the anti leakage trace index	CTI	UL746	PLC4
Leakage Trace Index		IEC60112	125	V
Volume resistance value		ASTM D-257	4×1016	Ω.cm
Dielectric constant	1MHz	ASTM D-150	3.9
Dissipation coefficient	1MHz	ASTM D-150	0.0014
Dielectric breakdown strength		ASTM D-149	16	KV/mm
Thermal conductivity		自定标准	0.27	W/m.K
Dielectric constant		ASTM D150/IEC 60250	3.90

Processing performance	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow	ASTM D-955	0.3	%
Shrinkage rate	Shrinkage rate	Across Flow	ASTM D-955	0.7	%
Dry conditions			120~150度 2.0～5.0hr
Processing temperature			270~300	°C
Processing temperature	Processing temperature			290~330	°C
Screw speed			100~150	rpm
Mold temperature			135~150	°C
pressure			1.00~20.0	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating		UL94	V-0

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength		内部方法	175	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.