Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | 23°C | ISO1183 | 1.99 | g/cm³ |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.50 | % |
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 0.25 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Yield,23°C | ISO527-2 | 105 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 0.90 | % |
| Bending modulus | 23°C | ISO178 | 19500 | Mpa |
| Bending stress | 23°C | ISO178 | 210 | Mpa |
| shear strength | 23°C | JISK7214 | 60.0 | Mpa |
| Friction coefficient 4 | | | 0.30 | |
| Taber abraser | 1000Cycles | ISO9352 | 70.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
| Melting temperature | | ISO11357-3 | 278 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.9E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | | IEC60243-1 | 21 | KV/mm |
| Dielectric constant 6 | 23°C,1MHz | IEC60250 | 5.30 | |
| Dissipation factor 5 | 23°C,1MHz | IEC60250 | 2E-03 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179 | 7.0 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 17 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 122 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | 0.72mm | UL94 | V-0 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| BarFlowLength6 | 320°C,1.00mm | 内部方法 | 8.00 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.