Material Description

Technical Data Sheet

Material Description

Material Properties:enhance environment?protection
Application Areas:Automotive Applications sporting goods
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Method	Test Result	Unit
density	ASTM D792/ISO 1183	1.66
Molding shrinkage rate	ASTM D955	0.2	%
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.02	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.00mm3	内部方法	0.80	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	内部方法	0.20	%
Water absorption rate	23°C,24hr	ISO62	0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	23°C	ISO527-2	200	Mpa
Tensile strain	Break,23°C	ISO527-2	1.6	%
Bending modulus	23°C	ISO178	15500	Mpa
Bending stress	23°C	ISO178	290	Mpa
shear strength	23°C	JISK7214	75.0	Mpa
Friction coefficient 5			0.25
Taber abraser	1000Cycles	ISO9352	50.0	mg
elongation at break		ASTM D638/ISO 527	1.6	%
tensile strength		ASTM D638/ISO 527	200	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	122
Bending modulus		ASTM D790/ISO 178	15.5	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	290	kg/cm²(MPa)[Lb/in²]
IZOD notch impact strength		ASTM D256/ISO 179	11	kg·cm/cm(J/M)ft·lb/in
IZOD notch impact strength	IZOD notch impact strength		ASTM D256/ISO 179	45	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	V-0
Hot deformation temperature		ASTM D648/ISO 75	>260	℃（℉）
melting point			278	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	2.3	mm/mm.℃
Linear coefficient of thermal expansion	TD	ISO11359-2	3.1E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	260	°C
Melting temperature		ISO11357-3	278	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	2.3E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	1E+16	ohms·cm
Dielectric strength		IEC60243-1	25	KV/mm
Dielectric constant 6	23°C,1MHz	IEC60250	3.60
Dissipation factor 6	23°C,1MHz	IEC60250	2E-03
Dielectric constant		ASTM D150/IEC 60250	3.6
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	45	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Sale	ISO2039-2	122

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.28mm	UL94	V-0

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength7	320°C,1.00mm	内部方法	150	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.