LCP SUMIKASUPER® E4008-BK SUMITOMO JAPAN

261

Unit Price:
$9925 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Chemical resistance Aging resistance Low viscosity dimensional stability
Application Areas:Automotive sector
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	内部方法	1.3	%
Shrinkage rate	Shrinkage rate	流量	内部方法	0.10	%
Water absorption rate	Saturation	ASTM D570	0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength		ASTM D638	150	Mpa
elongation	Break	ASTM D638	5.0	%
Bending modulus	23°C	ASTM D790	12300	Mpa
Bending modulus	Bending modulus	200°C	ASTM D790	6300	Mpa
bending strength	23°C	ASTM D790	139	Mpa
bending strength	bending strength	200°C	ASTM D790	39.0	Mpa
shear strength		ASTM D732	52.0	Mpa
Poisson's ratio		ASTM D785	0.49

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	1.8 MPa, Unannealed	ASTM D648	313	°C
Linear coefficient of thermal expansion	Flow : 150°C	内部方法	1.4E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 150°C	内部方法	6.2E-5	cm/cm/°C
thermal conductivity		JIS R2618	0.57	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		ASTM D257	1.0E+15	ohms·cm
Dielectric constant	1 kHz	ASTM D150	4.50
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.90
Dissipation factor	1 kHz	ASTM D150	0.018
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.034
Arc resistance		ASTM D495	130	sec
Leakage Trace Index		IEC 60112	145	V

injection	Test Result	Unit
drying temperature	130	°C
drying time	4.0 到 24	hr
Temperature at the rear of the barrel	330 到 350	°C
Temperature in the middle of the barrel	350 到 370	°C
Temperature at the front of the material cylinder	370 到 390	°C
Spray nozzle temperature	370 到 390	°C
Processing (melt) temperature	380	°C
Mold temperature	40 到 160	°C
Injection pressure	120 到 160	Mpa
Injection speed	中等偏快
Maintain pressure	40.0 到 60.0	Mpa
Back pressure	1.00 到 5.00	Mpa
Screw speed	50 到 100	rpm

Impact performance	Test Condition	Test Method	Test Result	Unit
Non notched cantilever beam impact	6.40 mm	ASTM D256	520	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	91

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.30 mm, NC, BK	UL 94	V-0
Extreme Oxygen Index		ISO 527-1,-2(JIS K7161,7162)	48	%
Soldering Resistance		内部方法	330	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.