PC/ABS CA1560 NA0500 YANTAI WANHUA
140
- Unit Price:
- $2272 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate flow | 2.0mm | ASTM D995 | 0.5-0.7 | % |
| Network Finance Index | 260℃5kg | ASTM D1238 | 19 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural modulus | 2.0mm/min | ASTM D790 | 2200 | Mpa |
| Elongation at break | 50mm/min | ASTM D638 | 50 | % |
| Cantilever beam gap impact | 23℃ | ASTM D256 | 550 | J/m |
| —30℃ | 450 | J/m | ||
| Tensile modulus | 1.0mm/min | ASTM D638 | 2400 | Mpa |
| tensile strength | 50mm/min | ASTM D638 | 55 | Mpa |
| bending strength | 2.0mm/min | ASTM D790 | 85 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa 120℃/hr | ASTM D648 | 100 | °C |
| Vicat softening temperature | 120℃/hr 50N | ASTM D1525 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | ASTM D257 | 10000000000000000 | Ω.cm | |
| Surface resistance | ASTM D257 | 10000000000000000 | Ω |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.