PC/ABS CYCOLOY™ CX7240-7T1D193 SABIC INNOVATIVE NANSHA
126
- Unit Price:
- $5973 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.20 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.10 | % | |
| Melt flow rate | 260°C/2.16 kg | ASTM D1238 | 18 | g/10 min |
| Molten Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 15.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.40 到 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | -- 5, 6 | ISO 178 | 96.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 104 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 65.0 | Mpa |
| Yield | ISO 527-2/50 | 65.0 | Mpa | |
| Break 3 | ASTM D638 | 58.0 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa | |
| Tensile modulus | -- 2 | ASTM D638 | 2600 | Mpa |
| -- | ISO 527-2/1 | 2600 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 4.1 | % |
| Yield | ISO 527-2/50 | 4.0 | % | |
| Break 3 | ASTM D638 | 100 | % | |
| Break | ISO 527-2/50 | 90 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2500 | Mpa |
| -- 5 | ISO 178 | 2500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ASTM D152511, ISO 306/B5011 | 110 | °C |
| -- | ISO 306/B120 | 113 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 7.5E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.5E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.20 | W/m/K | |
| RTI | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 100 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 89.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 99.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10 | ISO 75-2/Af | 93.0 | °C | |
| Ball Pressure Test | 73 to 77°C | IEC 60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 0.800 mm, in Oil | IEC 60243-1 | 35 | KV/mm |
| 1.60 mm, in Oil | IEC 60243-1 | 25 | KV/mm | |
| 3.20 mm, in Oil | IEC 60243-1 | 17 | KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 3 | ||
| High arc combustion index (HAI) 12 | UL 746 | PLC 0 | ||
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 90 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 250 到 300 | °C | ||
| Mold temperature | 60 到 85 | °C | ||
| Hopper temperature | 60 到 80 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Temperature at the rear of the barrel | 230 到 280 | °C | ||
| Temperature in the middle of the barrel | 240 到 290 | °C | ||
| Temperature at the front of the material cylinder | 250 到 300 | °C | ||
| Spray nozzle temperature | 250 到 300 | °C | ||
| Exhaust hole depth | 0.030 到 0.075 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 65.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 | °C |
| 0.75 mm 13 | IEC 60695-2-12 | 960 | °C | |
| Extreme Oxygen Index | ISO 4589-2 | 34 | % | |
| Hot filament ignition temperature | 0.75 mm 13 | IEC 60695-2-13 | 775 | °C |
| 1.0 mm | IEC 60695-2-13 | 825 | °C | |
| 1.5 mm 13 | IEC 60695-2-13 | 775 | °C | |
| 3.0 mm | IEC 60695-2-13 | 800 | °C | |
| 3.0 mm 13 | IEC 60695-2-13 | 775 | °C | |
| UL flame retardant rating | 0.60 mm | UL 94 | V-1 | |
| 0.75 mm | UL 94 | V-0 | ||
| 1.5 mm | UL 94 | 5VB | ||
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.